Abstract:Ti-2Al-2.5Zr alloy with hcp structure is a kind of structural materials used under low temperature condition, e.g. pipeline system of liquid hydrogen and liquid oxygen in missile engine. It is usually serviced in condition of severe low temperature and dynamic loading. Deformation twinning is a common and important plastic deformation mode in the hexagonal close-packed alloy., but will be severely restricted as the grain is refined from tens of microns to a few microns. On the other hand, twinning has a low sensitivity to temperature, consequently becomes a favorable deformation mode at low temperature in comparison with dislocation slip. The objective of this work is to study the coupling effect of grain refinement and testing temperature on twinning behavior and the low-cycle fatigue behavior of Ti-2Al-2.5Zr.Symmetrical push-pull low-cycle fatigue (LCF) tests were performed on Ti-2Al-2.5Zr with grain size of about 5 pm at room temperature (RT) and low temperature (77 K). The results show that the alloy exhibits the higher ductility and the longer low-cycle fatigue life at 77 K than those at RT. The cyclic stress response curves show that the cyclic softening occurs at the low strain amplitudes of 0.5% and 1.0%. However, as strain amplitude increased to 1.5% and 2.0%, cyclic stress saturation appeared. When testing temperature declined to 77 K, the cyclic hardening was observed at all four strain amplitudes. The degree of cyclic hardening increases as the strain amplitude rises. The fractography analyses suggest that transgranular fracture with well-developed fatigue striations is the predominant failure mode. The amount of secondary cracks is much higher in the alloys deformed at RT than that at 77 K. TEM examination reveals that deformation twins become more active. The primary types of twinning are {10 (1) over bar1} and {11 (2) over bar1}. The typical deformation microstructures consist of individual dislocation lines together with the tangled dislocation at the low strain amplitudes of 0.5% and 1.0%. As the strain amplitude increased to 1.5% and 2.0%, {10 (1) over bar0} prismatic slip and {11 (2) over bar1} pyramidal slip were simultaneously activated, the subgrain and dislocation cells were formed. At 77 K and strain amplitude of 2.0%, the parallel dislocation bands distribute along prismatic plane. As the strain amplitude increased to 4.5%, mutua l perpendicular dislocation lines appeared. The improvement of fatigue life of Ti-2Al-2.5Zr at 77 K is attributed to the constraint of inhomogeneous slip and the activation of deformation twinning.

Cyclic deformation behaviour of commercially pure titanium at cryogenic temperature

Low Cycle Fatigue Behavior Of Commercial Purity Titanium At Cryogenic Temperature

Tensile and low-cycle fatigue behavior of commercially pure titanium and Ti–5Al–2.5Sn alloy at 293 and 77 K

Flow Behavior and Microstructure Evolution of TB8 Alloy During Hot Deformation Process

Twinning induced plasticity in commercially pure titanium at low temperature

Mechanical Behavior and Deformation Modes of Commercially Pure Titanium under Impact Tensile Load

Twinning Behavior and Its Effect on Mechanical Behavior of Commercial Titanium at Cryogenic Temperature

Toughening of Titanium Alloys by Twinning and Martensite Transformation

Constitutive Model and Microstructure Evolution of a Novel TG6 High-Temperature Titanium Alloy during Hot Deformation

Strong Strain Hardening Induced by {11–22} Twins of Hexagonal Titanium upon Low-Temperature Deformation Along the Transverse Direction

Monotonic and cyclic behavior of Ti–2.5Cu alloy at room temperature (293 K) and at 77 K

LOW CYCLE FATIGUE BEHAVIORS AND MICROSTRUCTURES OF Ti–2Al–2.5Zr WITH FINE GRAIN AT RT AND 77 K

The High-Temperature Deformation Behavior of As-Cast Ti90 Titanium Alloy

Role of the Pulse Current Duty Cycle during Titanium Tension

Cyclic twins in high-purity titanium single crystals

Tensile and Low-Cycle Fatigue Behaviors of Commercially Pure Titanium Containing Γ Hydrides

Mechanical Behavior and Deformation Mechanisms of Ti–2.5Cu Alloy Reinforced by Nano-Scale Precipitates at 293 and 77 K

Cyclic Deformation and Microcrack Initiation During Stress Controlled High Cycle Fatigue of a Titanium Alloy

Tensile Properties and Deformation-Fracture Behavior of Ti-6Al-4V Alloy at Cryogenic Temperature

Flow Softening and Microstructural Evolution of TC11 Titanium Alloy During Hot Deformation

Effects of Thermal Cycling on Tensile Properties of Ti-6Al-4V Alloy at Room and Cryogenic Temperatures