Abstract:The fast exhaustion of the fossil fuels has led to an imperious need for more energy-efficient and environmentally friendly strategies to develop the carbon materials with high structural efficiency and multi-functional integration. Sucrose represents a promising biomass source for obtaining the carbon foams. However, the uncontrolled foaming restricts the preparation and performance of the efficient sucrose-based carbon foams. Herein, a novel route of template-free mechanical foaming-gel has been reported to fabricate the robust and multifunctional sucrose-derived carbon foams with the hierarchical porous structure. The pore structure and porosity could be flexibly controlled by tuning the sucrose concentration during the mechanical stirring process. The synergy between sucrose and epoxy hydrogel as a network skeleton endowed the carbon foams with a high carbon yield (44.7%) and optimal specific mechanical properties. The carbon foams after heat treatment at 1200 ?degrees C displayed a low density (0.089-0.195 g/cm(3)) and a high compression strength (1.02-4.93 MPa). The foams also exhibited excellent heat insulation performance and flame retardancy. The thermal conductivity of the carbon foam with a density of 0.089 g/cm(3) was as low as 0.092 W/m.K at room temperature and 0.269 W/m.K at 1200 ?degrees C under argon atmosphere. Furthermore, the carbon foams revealed a high oil absorption capacity, together with an optimal recyclability on combustion. Meanwhile, the foams also maintained super hydrophobicity after immersion in acidic, alkaline and salty media for 120 days. The developed strategy could not only realize the preparation of the energy-efficient and environmentally-friendly bio-carbon foams with a reliable self-adaptability to the extreme environments, but also exhibited promising universality and flexibility in designing the carbon materials for applications in aerospace and oil spill cleanup.

Sisal fibers reinforced soybean oil-based plastic foam

Preparation and Characterization of Novel Rigid Polyurethane Foams by Epoxidized Soybean Oil

Polyurethane Rigid Foams Formed from Different Soy-Based Polyols by the Ring Opening of Epoxidised Soybean Oil with Methanol, Phenol, and Cyclohexanol

Synthesis, Characterization and Properties of Soybean Oil-Based Polyurethane

Synthesis Of Soy-Polyols Using A Continuous Microflow System And Preparation Of Soy-Based Polyurethane Rigid Foams

The Thermal and Combustion Properties of Soybean Oil Phosphate-Based Polyurethane Foam Composites Containing Polyol of Etidronic Acid

Synthesis and Characterization of Epoxidized Silkworm Pupae Oil and Its Application as Polyvinyl Chloride

Plastic/Natural Fiber Composite Based on Recycled Expanded Polystyrene Foam Waste

Design and development of natural fibre reinforced syntactic foams for enhanced mechanical and acoustic capabilities

Soy polyol-based polyurethane modified by raw and silylated palygorskite

Preparation of Bio-Based Foams with a Uniform Pore Structure by Nanocellulose/Nisin/Waterborne-Polyurethane-Stabilized Pickering Emulsion

Preparation and Characteristics of Biocomposites Based on Steam Exploded Sisal Fiber Modified with Amphipathic Epoxidized Soybean Oil Resin.

Preparation and characterization of bioplastics from silylated cassava starch and epoxidized soybean oils

The Influence of Environmentally Friendly Plasticizer on the Bio-Durability of Wood Plastic Composites

Synthesis and characterization of alkoxy silane modified polyurethane wood adhesive based on epoxidized soybean oil polyester polyol

Phosphorus and nitrogen-containing soybean oil polyols: Effect on the mechanical properties and flame retardancy of polyurethane foam

Controllable Synthesis of a Robust Sucrose-Derived Bio-Carbon Foam with 3D Hierarchical Porous Structure for Thermal Insulation, Flame Retardancy and Oil Absorption

Preparation of bio‐based soybean oil polyol modified 3630 polyol‐based rigid polyurethane foam and its improved thermal stability, flame retardant, and smoke suppression performances

Processing and properties of rigid polyurethane foams based on bio-oils from microwave-assisted pyrolysis of corn stover