Abstract:This paper is to study the influence of sulphate corrosion on the mechanical behaviors of concrete, especially concrete corrosion under actual corrosion environment. This study investigated different immersion methods for concrete in a corrosion environment, and different strengths of concrete specimens with contents of sodium sulphate and magnesium chloride of 10.36% and 12.00%, respectively. Strength tests were performed on the specimens for the different immersion methods of full immersion, half-immersion, and dry-wet cycles, and with different strengths for the concrete of C20, C35, and C50. To study the internal mechanisms of the corrosion of concrete with different immersion methods and different strengths, a microscopic pore structure test was conducted. The field tests were performed after 12 years to evaluate the long term performance of the concrete under the actual environmental conditions. The test results show that full immersion mainly led to chemical corrosion, half immersion led to double damage from salt crystallization and chemical corrosion, and dry-wet cycles accelerated the corrosions of the salt crystallization and chemical corrosion. The higher the strength of concrete, the better its resistance to the sulphate corrosion. In comparison with the strength of the concrete before corrosion, field test results show that the strength of uncorroded concrete after 12 years is increased by 9.5% and the strength of corroded concrete after 12 years is reduced by 56.2%. The results of the strength tests and pore structure tests show that sulphate has a significant impact on concrete strength after 12 years of field tests. This study will contribute to improve long-term performance of the concrete, provide guidance for concrete structure design in corroded areas, and suggested that increasing attention should be paid to the effects of sulphate on concrete performance.

CURRENT STUDY OF THE INFLUENCE OF INORGANIC SALT ON DURABILITY OF CONCRETE

Deterioration characteristics of the bond between reinforcement and concrete subjected to freezing-thawing cycles and steel corrosion

Effect of Inorganic Salts on Surface Tension of Solutions and Properties of Concrete

Effect of Chlorine Salt on Durability of Mineral Admixture Concrete under Different Conditions

Analysis of durability for sea dam foundation

An Experimental Study on Relationship among Water Sorptivity, Pore Characteristics, and Salt Concentration in Concrete

Effect of Inorganic Salts on Pore Structure of Cement Paste

Experimental study on the capillary absorption of cement-based materials and analysis of influencing factors

Meso-scale Mechanical Deterioration of Mortar Due to Sodium Chloride Attack

Study on Relation Between Early-age Performance of Concrete and Its Durability

Concrete Admixed with Modified Auxiliary Cementing Materials for Real Sea Service

Optimal Design and Performance of Concrete with Function Component in Marine Environment

Effects of Cyclic Seawater Exposure on the Mechanical Performance and Chloride Penetration of Calcium Sulfoaluminate Concrete

Experimental Research on Durability of Concrete Made by Seawater and Sea-Sand

Research on Performance Deterioration of Internally Cured Pavement Concrete under the Coupling Effect of Salt Freeze-Thaw

Recent durability studies on concrete structure

Influence mechanisms under different immersion methods and different strengths of concrete in corrosive environments, and verification via long-term field test

Study on the deterioration of concrete performance in saline soil area under the combined effect of high low temperatures, chloride and sulfate salts

Comprehensive assessment of the durability deterioration of asphalt pavement in salt environment: A literature review

A Research on Durability Degradation of Mineral Admixture Concrete

Study of the influence of seawater and sea sand on the mechanical and microstructural properties of concrete