Abstract:Spartina alterniflora activated carbon (SAAC) was prepared by chemical activation with potassium hydroxide. The effects of four preparation variables: carbonization temperature, KOH:char impregnation ratio, activation temperature, and activation time on the iodine and p-nitroaniline adsorption onto the SAAC samples were investigated. Taguchi experimental design method was applied to optimize the preparation of SAACs. Optimized parameters were carbonization temperature of 450°C, impregnation ratio of 3:1, activation temperature of 800°C, and activation time of 90min, respectively. The surface characteristics of the SAACs were examined by pore structure analysis and scanning electron microscopy (SEM). Pore structure analysis showed that micropores constitute 86.75% of the porosity of the SAAC prepared at optimized conditions (SAAC-1) with a large pore volume of 1.374cm3/g, and the BET surface area is up to 2825m2/g. The adsorption equilibrium, kinetics and mechanism of p-nitroaniline onto SAAC-1 were carried out to investigate its adsorption ability. The results showed that the maximum adsorption capacity for p-nitroaniline was approximately 719mg/g. The pseudo-second-order model was found to explain the adsorption kinetics most effectively. The intraparticle diffusion played an important role in the adsorption and primarily controlled the adsorption rate. The negative change in free energy, negative change in entropy, and negative change in enthalpy indicated that the adsorption was a spontaneous and exothermic process, which was primarily driven by enthalpy change. The findings indicated that the microporous S. alterniflora activated carbon with high surface area is a potential high effective absorbent for p-nitroaniline removal from aqueous solutions.

ADSORPTION ISOTHERM OF P-Nitroanilne ONTO ACTIVATED CARBON PREPARED FROM SPARTIONA ALTERNIFLORA

Adsorption Behavior and Influence Factors of P-Nitroaniline on High Surface Area Activated Carbons Prepared from Plant Stems

Adsorption Kinetics of P-Nitroaniline Onto Microporous Carbon Activation with KOH

Optimization of Preparation of Microporous Activated Carbon with High Surface Area from Spartina Alterniflora and Its P-Nitroaniline Adsorption Characteristics

Preparation of high surface area microporous carbons and their adsorption of nitroaniline

Adsorption of P-Nitroaniline from Aqueous Solutions Onto Activated Carbon Fiber Prepared from Cotton Stalk.

Equilibrium, Kinetic and Thermodynamic Studies on the Adsorption of 2-Nitroaniline Onto Activated Carbon Prepared from Cotton Stalk Fibre.

Adsorption of Nitrous Oxide on Activated Carbons

Kinetics and Mechanism Studies of P-Nitroaniline Adsorption on Activated Carbon Fibers Prepared from Cotton Stalk by NH4H2PO4 Activation and Subsequent Gasification with Steam

Adsorption of P-Nitrophenol from Aqueous Solutions Onto Activated Carbon Fiber

Adsorption Behavior of p-Nitrophenol from Water onto Activated Carbon Fiber

Enhanced adsorption of p-nitroaniline from water by a carboxylated polymeric adsorbent

Adsorption Characteristics Of Nitrobenzene Onto Powdered Activated Carbon

ADSORPTION BEHAVIOR OF P-NITROANILINE ON MACROPOROUS POLYMER AND ITS APPLICATION

Kinetics and equilibrium adsorption study of p-nitrophenol onto activated carbon derived from walnut peel

Preparation, characterization and adsorption performance of high surface area biomass-based activated carbons

Nitrogen-Rich Polyaniline-Based Activated Carbon for Water Treatment: Adsorption Kinetics of Anionic Dye Methyl Orange

Adsorption of Naphthalene Onto a High-Surface-area Carbon from Waste Ion Exchange Resin

Kinetics of adsorption of 2,4-dichlorophenol by nitrogen doping activated carbon

Super facile one-step synthesis of aromatic amine waste residue derived N-rich porous carbon for hyper efficient p-nitrophenol adsorption

High adsorption of methyl orange by nitrogen-doped activated carbon derived from kraft lignin via self-activation