Abstract:A cheap cellulose-derived solid acid catalyst (Cellulose-SO3H), containing SO3H groups (1.69 mmol/g), was successfully prepared through sulfonation of incompletely carbonized cellulose. Various preparation variables exerted remarkable effects on the catalytic activity of the prepared catalyst, and the optimal preparation conditions were found as follows: carbonization at 400 degrees C for 15 h and subsequent sulfonation at 150 degrees C for 15 h. The resulting catalyst showed significantly higher activity for esterification of oleic acid with methanol than several typical solid acid catalysts (niobic acid, amberlyst-15, and sulfated zirconia). The Cellulose-SO3H catalyst was capable of efficiently catalyzing esterification of other higher fatty acids (palmitic acid and stearic acid) with methanol to the corresponding fatty acid methyl esters (biodiesel). Moreover, the conversion of waste oils containing 27.8% free fatty acids to biodiesel catalyzed by Cellulose-SO3H was investigated. It was found that the optimal molar ratio of methanol to oil, catalyst amount, reaction temperature, and reaction time were 25, 10% (based on the mass of waste oil), 85 degrees C, and 10 h, respectively. Under the optimal reaction conditions, the yield of biodiesel obtained catalyzed by Cellulose-SO3H was much higher than that by the above-mentioned three typical catalysts. Cellulose-SO3H still retained above 90% of its original catalytic activity even after 30 cycles of successive re-use, indicating excellent operational stability. It can be clearly seen that the Cellulose-SO3H catalyst displays tremendous potential for biodiesel production.

Biodiesel Production from Acidified Soapstocks Using a Biomass - Based Carbonaceous Catalyst

Synthesis of biodiesel from acidified soybean soapstock using a lignin-derived carbonaceous catalyst

Soft-template synthesis of sulfonated mesoporous carbon with high catalytic activity for biodiesel production

Sulfonic-acid-functionalized Lignin-Derived LC900@SO3H: A Promising Catalyst for the Efficient Production of Biodiesel Via the Esterification of Oleic Acid

Sulfonic-acid-functionalized lignin-derived LC900@SO 3 H: A promising catalyst for the efficient production of biodiesel via the esterification of oleic acid

Biodiesel production from waste oil feedstocks by solid acid catalysis

Biodiesel Production Via Transesterification of Soybean Oil Using Acid Catalyst in Co2 Expanded Methanol Liquids

Highly efficient procedure for the synthesis of biodiesel from soybean oil

Preparation of Cellulose-Derived Solid Acid Catalyst and Its Use for Production of Biodiesel from Waste Oils with High Acid Value

Esterification of Oleic Acid to Biodiesel Catalyzed by a Highly Acidic Carbonaceous Catalyst

Transesterification of Vegetable Oil to Biodiesel Using a Heteropolyacid Solid Catalyst

Study on Biodiesel from Cotton Seed Oil by Using Heterogeneous Super Acid Catalyst SO42−/ZrO2

A Highly Active Bagasse-Derived Solid Acid Catalyst with Properties Suitable for Production of Biodiesel.

A Highly Effective Biomass-Derived Solid Acid Catalyst for Biodiesel Synthesis Through Esterification

Novel Biodiesel Production Technology from Soybean Soapstock

Biodiesel Production from Esterification of Oleic Acid by a Sulfonated Magnetic Solid Acid Catalyst

Biodiesel production from waste cooking oil using a heterogeneous catalyst from pyrolyzed rice husk

Synthesis of Biodiesel from Waste Vegetable Oil with Large Amounts of Free Fatty Acids Using a Carbon-Based Solid Acid Catalyst

Biodiesel Production from Vegetable Oil Using Heterogenous Acid and Alkali Catalyst

Preparation of solid acid catalyst from glucose-starch mixture for biodiesel production

Microwave-assisted biodiesel production using –SO3H functionalized heterogeneous catalyst derived from a lignin-rich biomass