Abstract:To determine how the performance of concrete changes after initial load damage and salt freezing, concrete samples were first subjected to loading and unloading, and were then put into salt solutions to carry out rapid freeze-thaw cycle (FTC) experiments. Salt solutions were created based on the saline soil of western Jilin, China, for use in salt freeze-thaw testing. This determined the change law of the compressive strength and the dynamic elastic modulus (DEM). Additionally, low-field nuclear magnetic resonance technology and a scanning electron microscope were applied to investigate the pore characteristics and microstructure of concrete samples after FTCs. This study found that when the concrete specimens were subjected to an initial load of 0.3f under 50 FTCs, the loss in the compressive strength increased by 24% when the concrete was subjected to freeze-thaw cycles in freshwater and increased by 24% when concrete was subjected to freeze-thaw cycles in a 6.8% composite salt solution compared with the specimens without the initial load. When the concrete was subjected to FTCs in a 6.8% composite salt solution 50 times, the loss in the compressive strength increased by 110% for concrete without an initial load and increased by 109% when the concrete was subjected to an initial load of 0.3f compared with the specimens under FTCs in freshwater. The persistent effect of the FTCs also aggravated chloride ion erosion in the concrete, which gradually reduced the concrete's permeability resistance. Internal pores in the concrete, especially the proportion of above-medium-sized pores, gradually increased along with the increase in the number of FTCs. There is a good linear correlation between the change rule of compressive mechanical properties and the change rules of mass, DEM, and pore characteristics inside the concrete under rapid FTCs in different salt solutions.

Experiment of properties deterioration of air-entrained concrete in seawater-aggressive and freeze-thaw environment

Deterioration characteristics of the bond between reinforcement and concrete subjected to freezing-thawing cycles and steel corrosion

Experimental Study and Mechanism Analysis on Frost Resistance of Normal Performance Concrete under Different Environments

Behavior of Air-Entrained Concrete after Freeze-Thaw Cycles

Meso-Scale Mechanical Deterioration Of Mortar Subjected To Freeze Thaw Cycles And Sodium Chloride Attack

Experimental Evaluation of the Concrete Damage and Pore Characteristics under Salt-Freezing Cycles

Deterioration of Concrete Freezing-Thawing in Different Salts Solution

Macroscopic and Mesoscopic Deterioration Behaviors of Concrete under the Coupling Effect of Chlorine Salt Erosion and Freezing–Thawing Cycle

FROST RESISTANCE OF CONCRETE IN SALT SOLUTION

Accelerating Tests For The Performance Deterioration Of Concrete Exposed To Chloride Media

Concrete Durability after Load Damage and Salt Freeze-Thaw Cycles

Experimental Research on Chloride Ingress into Concrete Exposed to Freeze-Thaw Cycles

Deterioration of concrete under the coupling action of freeze–thaw cycles and salt solution erosion

Effects of Cyclic Seawater Exposure on the Mechanical Performance and Chloride Penetration of Calcium Sulfoaluminate Concrete

Degradation Mechanism and Numerical Simulation of Pervious Concrete under Salt Freezing-Thawing Cycle

Experimental Study on Mechanical Properties and Pore Structure Deterioration of Concrete under Freeze–Thaw Cycles

Influence of the Coupling Action of Flexural Load and Freezing–Thawing on the Chloride Diffusion of Marine High-Performance Concrete

Study on the deterioration of concrete performance in saline soil area under the combined effect of high low temperatures, chloride and sulfate salts

Experimental studies on mechanical properties of concrete under freeze-thaw action

Degradation of mechanical properties of concrete caused by freeze-thaw action

Experimental Study on Compressive Property of Concrete Corroded by Seawater in Low-Temperate