Abstract:In this work, we developed a simple method for synthesizing CdSe/ZnSe/ZnS multishell quantum dots (QDs). CdSe/ZnSe core/shell QDs was synthesizd using one step injection of zinc precursor into the crude solution of the CdSe reaction system and then CdSe/ZnSe/ZnS core/shell/shell QDs were obtained by epitaxially growing a ZnS shell on the CdSe/ZnSe surface. Introducing a middle shell (ZnSe) sandwiched between CdSe core and ZnS outer shell allows considerably reduce strain inside nanocrystals because ZnSe have the lattice parameter intermediate to those of CdSe and ZnS. In comparison with the method reported previously, our synthesis method effectively simplifies the experimental operation, shortens the experimental period and reduces the waste of the chemcals. The annealing process was used to improve the fluorescence quantum yield of the QDs after the shell growth. The resulting CdSe/ZnSe/ZnS multishell QDs was further characterized in detail. Transmission electron microscopy indicated that the QDs are spherical and the shell is successfully coated on the surface of the CdSe QDs. The size of CdSe core is 2.8 nm, and the size of the CdSe cores with CdSe/ZnSe and CdSe/ZnSe/ZnS shells are determined to be 4 and 5 nm, respectively. The X-ray powder diffraction patterns suggested that the core (CdSe) and shell (ZnSe and ZnS) of the CdSe/ZnSe/ZnS QDs have a pure cubic phase. The luminescence properties of the QDs were investigated by means of photoluminescence and ultraviolet-visible absorption spectra. The results indicated the CdSe/ZnSe/ZnS QDs exhibit a high photoluminescence quantum yield. Besides, it can be seen that the absorption and photoluminescence bands shift to the red during the shell growth due to the large extension of the electronic wave function into the shell material. For the potential biological application, the CdSe/ZnSe/ZnS QDs were transferred into water phase from an organic phase by surface ligand exchange with mercaptopropionic acid. The water-soluble QDs with a quantum yield of about 17% have compatible functional chemical groups.

Depositing ZnS Shell Around ZnSe Core Nanocrystals in Aqueous Media Via Direct Thermal Treatment

Depositing a Zn<sub><i>x</i></sub>Cd<sub>1−<i>x</i></sub>S Shell around CdSe Core Nanocrystals via a Noninjection Approach in Aqueous Media

Synthesis and Characterization of Znse/Zns Core/Shell Nanocrystals by Aqueous Reflux Route

Facile Synthesis of Highly Luminescent Uv-Blue-Emitting Znse/Zns Core/Shell Nanocrystals in Aqueous Media

Synthesis and Characterization of ZnSe:Fe/ZnSe Core/shell Nanocrystals

Optical Properties of Monodisperse ZnSe:Mn/ZnS Core–Shell Nanocrystals Synthesized Via an Alkylthiol-Assisted Phosphine-Free Method

Preparation and Characterization of Znse Nanocrystals by A Microemulsion-Mediated Method

Synthesis of highly luminescent Mn:ZnSe/ZnS nanocrystals in aqueous media.

Hydrothermal synthesis of ZnSe nanoparticle

Synthesis and Optical Properties of Thiol Functionalized CdSe/ZnS (core/shell) Quantum Dots by Ligand Exchange

A room-temperature method for coating a ZnS shell on semiconductor quantum dots

An Aqueous Approach to ZnSe and CdSe Semiconductor Nanocrystals

Optimized synthesis of ZnSe nanocrystals by hydrothermal method

Passivated ZnSe Nanocrystals Prepared by Hydrothermal Methods and Their Optical Properties

Microwave-Assisted Aqueous Synthesis: A Rapid Approach to Prepare Highly Luminescent Znse(S) Alloyed Quantum Dots

Facile and Green Synthesis of Core–shell ZnSe/ZnS Quantum Dots in Aqueous Solution

Water-Based Route To Ligand-Selective Synthesis Of Znse And Cd-Doped Znse Quantum Dots With Tunable Ultraviolet A To Blue Photoluminescence

The Preparation of ZnSe Nanocrystals via Hydrothermal Process and Their Photoluminescent Characteristics

Facile Phosphine-Free Synthesis of CdSe/ZnS Core/Shell Nanocrystals Without Precursor Injection

Preparation and Photoluminescence of Water-Dispersible Znse Nanocrystals

Synthesis and Characterization of the CdSe/ZnSe/ZnS Multishell Quantum Dots