Abstract:This paper evaluates the shrinkage performance of concrete under complex internal constraint environments comprising steel plates, studs, and reinforcement to investigate their respective influence laws on the shrinkage performance of concrete. An early shrinkage model of concrete under complex internal constraints was established based on the theory of capillary tension, and the effects of steel plate, nails, and steel reinforcement on the shrinkage performance of concrete were theoretically analyzed. Six sets of concrete-constrained shrinkage tests and pore structure tests were then performed under different internal constraint conditions with the steel plate thickness, reinforcement diameter, and stud-related parameters (stud diameter, height, and spacing) as research variables. The test results demonstrate that the pore structure of concrete increases with the increase in the constraint coefficient, and that the increase in the pore structure will cause a decrease in the capillary pore stress, which is the driving force of concrete shrinkage. Its decrease will inevitably lead to a decrease in concrete shrinkage. By comparing the calculated values of the shrinkage model with the measured values, it is found that the average value of the prediction error is less than 15%, which reveals that the predicted values of shrinkage are in good agreement with the measured values and proves that the model can effectively predict the shrinkage of concrete that is restrained by steel plates, pins, and reinforcing bars.

Influence of Reinforcing Bars on Shrinkage Stresses in Concrete Slabs

Effects of Reinforcement Bar on Shrinkage Stress of Concrete

Influence of Steel Reinforcement on Shrinkge Stress of Concrete

Analytical model for critical corrosion level of reinforcements to cause the cracking of concrete cover

Analytical Model for the Bond Stress-Slip Relationship of Deformed Bars in Normal Strength Concrete

Analytical Prediction and Experimental Research on Shrinkage Cracking of Restrained Early-Age Concrete

Analysis of Shrinkage-Induced Stresses in Concrete Pavements

Damage Analysis and Cracking Model of Reinforced Concrete Structures with Rebar Corrosion

Numerical Analysis of Drying Shrinkage in Long Reinforced Concrete Structure

Early Shrinkage Modeling of Complex Internally Confined Concrete Based on Capillary Tension Theory

Analysis on the Cracking of Concrete Cover Due to Rebar Corrosion

Prediction of Corrosion-Induced Crack Width of Corroded Reinforced Concrete Structures

Influence of Steel Plates and Studs on Shrinkage Behavior and Cracking Potential of High-Performance Concrete

Cover Cracking Model in Reinforced Concrete Structures Subject to Rebar Corrosion

THEORETICAL INVESTIGATION TO CRACKING PREDICTION OF EARLY-AGE CONCRETE

Crack shape and rust distribution in corrosion-induced cracking concrete coupled with load

Influence of Flexural Loading on Chloride Ingress in Concrete Subjected to Cyclic Drying-Wetting Condition

Experimental Study on Cracking Property of Self-Compacting Concrete

Study of Model and Relevant Theory of Shrinkage Cracking of Concrete

Influence of Supporting Base Characteristics on Shrinkage-Induced Stresses in Concrete Pavements

Insight into Thermal Stress Distribution and Required Reinforcement Reducing Early-Age Cracking in Mass Foundation Slabs