Abstract:THIS STUDY investigates the stress, porosity, and composition of amorphous Ni-Mo-P electroless deposits obtained from typical acid (pH = 4.6) and alkaline (pH = 8.0) solutions, their effects on the corrosion performance of deposits in 5% NaCl, and the generation mechanism of stress and porosity. The results indicate that the deposit obtained at a certain pH and Na2MoO4 concentration has the best corrosion resistance in 5% NaCl. With the increase of Na2MoO4 concentration, the stress quickly changes from compressive to tensile, and the porosity increases. The higher the stress and porosity, the poorer is the corrosion resistance. When the Na2MoO4 concentration is about 0.05g/l, the deposit with the highest corrosion resistance, in neutral 5% NaCl, is easily obtained. The corrosion resistance in the long term was mainly governed by the stress of the deposits; the corrosion resistance in the short term was mainly governed by their porosity. When deposits have no porosity and at a low stress, amorphous Ni-Mo-P alloys with higher Mo contents have a better corrosion resistance; the phosphorous in the amorphous Ni-Mo-P films does not have an obvious influence on the corrosion resistance. Stresses were measured by X-ray analyser, and checked by appearance, after immersion in 5% HCl for 35 days. Corrosion performance was investigated by immersion corrosion tests, HNO3 corrosion blacking tests, porosity ferroxyl indicator tests, and the electrochemical corrosion technique.

Corrosion Resistance of Electroless Amorphous Ni-W-P Coating on 316X Stainless Steel

Corrosion Resistance of Electroless Amorphous Ni-W-P Coating on 316L Stainless Steel

Investigation of Corrosion Resistance in Stainless Steel 316L Alloy of Energy Separator by Electroless Plating (Ni-Zn-P)

Wear and Corrosion Properties of Crystalline Ni-W Alloy Coatings Prepared by Electrodeposition

Electroplating and Physicochemical Properties of Zinc–Nickel Alloy Coatings from Ammonium Oxalate Electrolytes

Corrosion resistance of electrolessly deposited Ni–P and Ni–W–P alloys with various structures

High Hardness and Wear Resistance Electroless Ni-P Deposits Without Heat Treatment

Preparation of Amorphous Nickel-Phosphorus Alloy Coating by Electroplating

Fabrication of a Robust Superhydrophobic Ni Coating with Micro–Nano Dual‐Scale Structures on 316L Stainless Steel

High Corrosion-Resistant Ni–P/Ni/Ni–P Multilayer Coatings on Steel

Electrochemical Behavior of (cr, W, Al, Ti, Si)N Multilayer Coating on Nitrided AISI 316L Steel in Natural Seawater

Effect of Electrolyte pH on Microstructure, Corrosion Behavior, and Mechanical Behavior of Ni-P-W-TiO2 Electroplated Coatings

Superior Protective Performance of Ni Cr Coating on Stainless Steel 316L in Pure, Oxygenated and Chlorinated Supercritical Water

Electrochemical Corrosive Behaviors of Fe-Based Amorphous/ Nanocrystalline Coating on Stainless Steel Prepared by HVOF-Sprayed

Corrosion Behaviors of Electroless Plating Ni–P Coatings Deposited on Magnesium Alloys in Artificial Sweat Solution

Optimization of the Electroplating Process for Amorphous Nickel- Phosphorus Alloy

Study on Electroless Plating Ni-W-P Ternary Alloy with High Tungsten from Compound Complexant Bath

Plating Bath Composition Optimization And Corrosion Resistance Of Ni-Sn-Mn Amorphous Coating Prepared By Electrodeposition

Corrosion Behavior of Ni-P-Nano-Al2o3 Composite Coating in the Presence of Anionic and Cationic Surfactants

Stress And Corrosion Performance Of Amorphous Ni-Mo-P Electroless Deposits

Study of Electroless Ni-Zn-P Alloy Plating from Acidic Bath