Abstract:Highly oriented titania nanotube (TN) arrays with {1 0 1} crystal face were prepared on the surface of titanium substrate by liquid chemical deposition method. The obtained titania samples were characterized by X-ray diffraction (XRD), atomic force microscope (AFM), scanning electron microscope (SEM), BET measurements, diffuse reflectance spectroscopy (DRS), and electron paramagnetic resonance (EPR) spin trap technique. Results indicate that the nanotubes grown in this study are well-aligned and organized into high-density uniform arrays. The typical dimensions of the hollow tube are ∼90 nm in outer diameter, ∼60 nm in inner diameter, ∼15 nm in wall thickness and ∼300 nm in height. The BET surface area of the obtained titania nanotube is 275 m2/g. The EPR signals reveal that hydroxyl radical (OH) species can be produced in the nanotube system, and no OH radical EPR signals were detected under dark and/or nanotube non-existing situations. The catalytic degradation of a textile azo dye, acid orange 7 (AO7), in aqueous solution with titania nanotube arrays electrode was carried out using photo-electrocatalytic (PEC) process, comparing with electrochemical process (EP) and photocatalytic (PC) process. A significant photo-electrochemical synergetic effect was observed, which is due to the efficient charge separation and transfer at the surface-interface of titania nanotube arrays. The kinetic constant of PEC degradation of AO7 using TN electrode was 48.7%, which is higher than that using P-25 TiO2 film and TiO2 particular film electrode. The enhanced degradation rate of AO7 using titania nanotube arrays could be attributed to their larger specific surface area and nanotubular structure with preferred reactive crystal face, which would increase their absorption capacity to the targeted substrates and the rate of surface-interface charge transfers in titania nanotube semiconductor redox systems.

Characterization of CNT/TiO2Electrode Prepared Through Impregnation with TNB and Their Photoelectrocatalytic Properties

Synthesis and Characterization of Cnt / Tio2 Photoelectrocatalytic Electrodes for Methlene Blue Degradation

Electro-Chemical Preparation of Tio2/Cnt Electrodes with Tnb Electrolyte and Their Photoelectrocatalytic Effect

Fabrication and characterization of photoelectrocatalytic electrodes of carbon nanotube/titanium oxide

Fabrication of CNT/TiO2 electrodes and their photoelectrocatalytic properties for methylene blue degradation

Synthesis of g-C3N4/Bi2O3/TiO2 composite nanotubes: enhanced activity under visible light irradiation and improved photoelectrochemical activity

Photoelectrocatalytic Degradation of Dyes in Aqueous Solution Using CNT/TiO2Electrode

Fabrication and Electro-Photolysis Property of Carbon Nanotubes/Titanium Composite Photocatalysts for Methylene Blue

Optimization of Cds/Tio2 Nanotube-Array Composite Photocatalysts Prepared by Electrodeposition

Photocatalyst-coated Carbon Microtube Electrodes: Preparation and Characterization of Their Properties and Photocatalytic Degradation of Methylene Blue.

Synthesis of Co3O4/Ag/TiO2 Nanotubes Arrays Via Photo-Deposition of Ag and Modification of Co3O4 (311) for Enhancement of Visible-Light Photoelectrochemical Performance

Preparation and Photocatalytic Degradation of CNT/TiO₂ Composites Using MWCNT and Various Titanium Alkoxide Precursors

The Effect of Introduced Method of Titania and Applied Potential on the Photoelectrocatalytic Properties of Cnt/Tio(2)Electrodes

Preparation and Catalytic Properties of Pt/CNT/TiO2Composite

Synthesis and Characterization of CNT/TiO2 Composites Thermally Derived from MWCNT and Titanium(IV) N-Butoxide

Photocatalytic Decomposition Of Mb Solution By Cnt/Tio(2) Composites Prepared From Mwcnt And Titanium Source

Preparation of Cr/CNT/TiO 2 composites and influences of Cr particles on the photocatalytic activity under visible light

Fabrication and Photo-Electrocatalytic Properties of Highly Oriented Titania Nanotube Arrays with {1 0 1} Crystal Face

Formation of Tio2 Composites on Activated Carbon Modified by Nitric Acid and Their Photocatalytic Activity

Electro-chemical preparation of TiO2/ACF composites with TNB electrolyte anal their photocatalytic effect

Photocatalytic Degradation of Methylene Blue by CNT/TiO2Composites Prepared from MWCNT and Titanium N-Butoxide with Benzene