Microwave Sintering of Plasma-Sprayed Yttria Stabilized Zirconia Electrolyte Coating
Chao Zhang,Ga Zhang,Susanne Leparoux,Hanlin Liao,Cheng-Xin Li,Chang-Jiu Li,Christain Coddet
DOI: https://doi.org/10.1016/j.jeurceramsoc.2008.03.040
IF: 5.7
2008-01-01
Journal of the European Ceramic Society
Abstract:In this work, microwave (MW) was used to sinter atmospheric plasma-sprayed 8mol% yttria stabilized zirconia (YSZ) electrolytes coatings. Three types of coatings were studied: pure YSZ coating, 5wt% BaTiO3 filled YSZ coating and 10wt% BaTiO3 filled YSZ coating. Microstructures and ionic conductivities of as-sprayed and MW-sintered coatings were characterized. The results indicated that that the pure YSZ coating can hardly be sintered by the MW sintering and it can only be heated up to 900°C. For two composite coatings, BaTiO3 particles distributed in the composite coating act as a good MW susceptor and thereby, a good heat source for sintering YSZ matrix. After a MW sintering at 1450°C for about 30min, an obvious structural modification was noticed: the lamellar and columnar crystal features of as-sprayed plasma-sprayed YSZ coatings were modified to equiax crystal in the sintered coatings. Ionic conductivity of sintered 5wt% BaTiO3 filled YSZ composite coatings were elevated to about twice of as-sprayed coating. A further increase of BaTiO3 content to 10wt% in the composite coating enhanced the sintering efficiency, however, the ionic conductivity of composite coatings was decreased.