Preparation and Properties of Red Emitting Phosphor Gd2Mo3O9∶Eu3+ for White LEDs

Guo-you ZHANG,Xiao-xia ZHAO,Qing-yu MENG,Xiao-jun WANG
DOI: https://doi.org/10.3321/j.issn:1000-7032.2007.01.012
2007-01-01
Chinese Journal of Luminescence
Abstract:Eu3+-doped Gd2Mo3O9 was prepared by solid-state reaction route using Na2CO3 as flux and characterized by powder X-ray diffraction.According to X-ray diffraction,this material is belongs to tetragonal system.The effects of flux content and sintering temperature on the luminescent properties were investigated by emission and excitation spectra.The results showed that flux content and sintering temperature have impact effects on the luminescent properties,the optimized flux content and the best sintering temperature is 3% and 800 ℃,respectively.The excitation and emission spectra also show that this phosphor can be effectively excited by C-T band(280 nm),ultraviolet light 395 nm and blue light 465 nm.The wavelengths at 395 nm and 465 nm are nicely fitting in with the widely applied emission wavelengths of ultraviolet or blue LED chips.Integrated emission intensity of Gd2Mo3O9∶Eu is 2 times stronger than that of Y2O2S∶Eu3+ under 395 nm excitation.The Eu3+ doped Gd2Mo3O9 phosphor may be a better phosphor candidate for solid-state lighting applications.
What problem does this paper attempt to address?