Dynamic .GAMMA..RAR..ALPHA. Transformation During Hot Deformation in Iron-Nickel-Carbon Alloys.

H Yada,CM Li,H Yamagata
DOI: https://doi.org/10.2355/isijinternational.40.200
2000-01-01
ISIJ International
Abstract:Fe-6mass%Ni-(0.0008∼0.29)mass%C alloys were hot-deformed in torsion at 600-720°C (above the cooling transformation start temperatures A r3 ) after austenitization. An in-situ X-ray diffraction study revealed that γ→α transformation occurred during deformation in a wide range of condition, even above A p 3 (paraequilibrium γ→α transformation temperature). Corresponding to this transformation, apparent decrease in deformation stress from that expected for austenite was observed. Microstructural study of the specimens quenched after the deformation showed that a large amount of fine-grained ferrite was formed due to the deformation. The analysis of deformation stress and chemical driving-force of the transformation indicated that the transformation occurred in order to reduce the total energy of deformed material since the deformation of energy of α was revealed to be considerably smaller than that of γ and the amount of deformation energy saved by the transformation was shown to be much greater than the chemical energy consumed by the transformation at the tested temperatures.
What problem does this paper attempt to address?