Synthesis, Structure and Optical Properties of Novel Thermally Robust Dy3+-doped Ca9Sc(PO4)7 Phosphors for NUV-excited White LEDs
Haiyan Wu,Huimin Li,Lihong Jiang,Ran Pang,Su Zhang,Da Li,Guanyu Liu,Chengyu Li,Jing Feng,Hongjie Zhang
DOI: https://doi.org/10.1016/j.jre.2020.05.007
IF: 4.632
2020-01-01
Journal of Rare Earths
Abstract:The powder samples of Ca9Sc(PO4)(7):xDy(3+) white emitting phosphors were prepared via a solid state reaction technique. The Ca9Sc(PO4)(7):Dy3+ samples were researched by using the GSAS Rietveld refinement and X-ray diffraction (XRD) methods, and SEM images and elemental maps were recorded. Under 350 nm excitation, the emission spectra of Ca9Sc(PO4)(7):xDy(3+) samples have two obvious peaks and one weak peak at 484, 572 and 660 nm, corresponding to the characteristic electron transitions of (F-4(9/2) -> H-6(15/2), blue), (F-4(9/2) -> H-6(13/2), yellow) and (F-4(9/2) -> H-6(11/2), red), respectively. The concentration quenching effect, decay lifetime and thermal quenching of the as-synthesized Ca9Sc(PO4)(7):Dy3+ samples were researched systematically. The Ca9Sc(PO4)(7):0.02Dy(3+) phosphor possesses a good thermal stability, of which the emission intensity at 423 K can maintain 79% of the initial value (273 K). In addition, through the study of the chromaticity coordinates of the Ca9Sc(PO4)(7):0.02Dy(3+) phosphor, it is found that it is located in the white region, and the Commission Internationalede L'Eclairage (CIE) chromaticity coordinates are (0.339, 0.389). The above results show that Ca9Sc(PO4)(7):xDy(3+) phosphors can be excellent candidate material for applications in NUV-excited white LEDs. (C) 2020 Published by Elsevier B.V. on behalf of Chinese Society of Rare Earths.