The effect of Ca 2+ in Li 0.24+x La 0.59−x Ca x TiO 3 -LaPO 4 system

Huiyong Liu,Benren Liao,Fenyan Lian,Wenji Wang

DOI: https://doi.org/10.1007/BF02375971

IF: 2.961

2003-01-01

Ionics

Abstract:Li 0.2375+x La 0.5875−x Ca x TiO 3 -LaPO 4 fast ionic conductor was synthesized by high temperature solid-state reaction. A.C. impedance measurements show that the compositions of system have better conductivities in low doping content of Ca 2+ , but the conductivity goes down from 1.039·10 −4 Scm −1 to 1.173·10 −5 Scm −1 with increasing the content of Ca 2+ . The activation energy is about 20 kJ·mol −1 in the temperature range of 25–400 °C. X-ray powder diffraction shows that the doping Ca 2+ would not affect the structure of compositions in the system. The main phase is β-Li 0.24+x La 0.59−x Ca x TiO 3 perovskite solid solution, LaPO 4 as a second phase also can be found. With the increasing content of Ca 2+ (x>0.05), another phase CaTiO 3 appears obviously. IR measurement also indicates that the structure of compositions in the system would not be affected by Ca 2+ doping. The decomposition voltage of Li 0.24+x La 0.59−x Ca x TiO 3 -LaPO 4 keeps on 1.6 V.