Promising Strategy to Synthesize ZSM-5@Silicalite-1 with Superior Catalytic Performance for Catalytic Cracking Reactions
Hongyu Shen,Min Liu,Junjie Li,Xiujie Li,Sujuan Xie,Fucun Chen,Longya Xu,Xinwen Guo,Chunshan Song,Xiangxue Zhu
DOI: https://doi.org/10.1021/acs.iecr.1c01043
2021-06-21
Abstract:The core–shell with regular morphology was prepared through an innovative tandem synthesis strategy for the first time, which combined the insertion of almost all aluminum sites by organotemplate-free synthesis and the sequential crystallization of residual silica sites by organotemplate-oriented synthesis. Samples with different Si and Al distributions could be synthesized by adjusting the tandem synthesis process, including temperature, time, Na<sub>2</sub>O/SiO<sub>2</sub>, etc. The obtained Si-rich-ZSM-5 and conventional C-ZSM-5 with a similar Si/Al ratio but different Al distributions, which were demonstrated by X-ray fluorescence (XRF), X-ray photoelectron spectroscopy (XPS), Transmission electron microscopy (TEM), and 1,3,5-triisopropylbenzene catalytic cracking analysis, were employed in <i>n</i>-hexane catalytic cracking reaction. Si-rich-ZSM-5 showed a higher stability with a <i>n</i>-hexane conversion of 57.7% at 100 h compared with that of C-ZSM-5 (24.6%), which was attributed to its inactive outer shell. Besides, a high para-xylene selectivity in xylene for the Si-rich-ZSM-5 catalyst was obtained. Hence, this study provides a simple and cost-effective strategy to fabricate highly stable catalysts for cracking reactions.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.iecr.1c01043?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.iecr.1c01043</a>.Discussions of materials and synthetic methods used, tables of synthesis conditions, physicochemical properties, and number of acid sites of different ZSM-5 samples, and figures of SEM and TEM images, XRD patterns, N<sub>2</sub> adsorption–desorption isotherms, Al concentration, TEM-EDS analyses, optical photographs of the used catalysts, thermogravimetric curves, selectivity with TOS, <i>n</i>-hexane uptake kinetics curves, and product distributions with time on stream (<a class="ext-link" href="/doi/suppl/10.1021/acs.iecr.1c01043/suppl_file/ie1c01043_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
engineering, chemical