Abstract:A newly developed method for the formation of nanowires by self-aggregation of nanoparticles is presented in this paper. Co3C, Co-rich, and Ni nanoparticles dispersed on holey carbon grids are inserted in a vacuum oven and are co-annealed with PolyChloroTriFluoroEthylene (PCTFE) at 375 degrees C. No external electric or magnetic fields were applied. High resolution electron microscopy (HREM) was extensively used to determine the shape, size distribution and crystallographic phase of the starting and produced materials. Interestingly, after an annealing circle of 72 hours, the nanoparticles seem to self-agglomerate into nanowires which have diameters in the 5-20 nm range and lengths exceeding at cases 1 micron. The diameter of the produced wires is in the same range as the diameter of the initial nanoparticles, further supporting the notion that the nanowires have formed out of nanoparticle agglomeration. Close inspection of nanowire HREM images shows that the core structure of nanowires wider than approximately 11 nm resembles linked nanoparticles. Phase identification performed using the HREM images reveals the core is of the same phase/material as the starting nanoparticles. Since nanowires appear to form over holes on the holey carbon grid, a base growth mechanism is proposed. The fluorocarbon vapour decomposes over the transitional metal nanoparticles and carbon tubules start growing. The nanoparticles appear to be trapped inside the tubules where their close proximity enhances their fusion into a continuous core. At the studied temperature, the nanoparticle fusion is seen to be limited by the size of the nanoparticles manifested by continuous cores only in the thin nanowires. The process presented here shows that nanoparticles can spontaneously self-align into nanowires in a way and to an extent never reported before. Therefore there is certainly scope for studying this method further to reveal more information about the catalytic action of transitional metals on hydrocarbons and the exact nanowire formation mechanism. Although it is currently a matter of speculation, this process might lead to the effortless growth of nanowires at particular places when building miniature circuits.

The formation mechanism of the coaxial carbon–metal nanowires in a chemical vapor deposition process

Spontaneous self-agglomeration of magnetic nanoparticles into nanowires

Fabrication of a Co-Mo-Based Metal-Organic Framework for Growth of Double-Walled Carbon Nanotubes

Growth and Nanoscale Magnetic Properties of Ferromagnetic Nanowire Encapsulated Inside Carbon Nanotubes

Encapsulated Nanowires Formed by Nanotube-Assisted Oriented Attachment

Thin-Film Metal Catalyst For The Production Of Multi-Wall And Single-Wall Carbon Nanotubes

Compound growth and microstructure of carbon nanotube

Formation and Growth Mechanism of Dissimilar Coiled Carbon Nanotubes by Reduced-Pressure Catalytic Chemical Vapor Deposition

Influence of Mo on the Fe:Mo:C nano-catalyst thermodynamics for single-walled carbon nanotube growth

Formation of multi-walled carbon nanotubes by catalytic chemical vapour deposition using zeolite encapsulated nanocrystalline cobalt oxides

Fabrication and Growth Mechanism of Carbon Nanotubes by Chemical Vapor Deposition

Morphogenesis of Branched Coaxial Nanorods Formed in Supercritical Carbon Dioxide

TEM Investigation on the Growth Mechanism of Carbon Nanotubes Synthesized by Hot-Filament Chemical Vapor Deposition.

Direct Growth of Carbon Nanotube Junctions by a Two-Step Chemical Vapor Deposition

In-situ preparation of carbon nanotubes on CuO nanowire via chemical vapor deposition and their growth mechanism investigation

Awl‐like HfC Nanowires Grown on Carbon Cloth Via Fe‐catalyzed in a Polymer Pyrolysis Route

Formation of catalyst particles for carbon nanocoil growth.

Template Synthesis and Growth Mechanism of Metal Nanowire/carbon Nanotube Heterojunctions.

Formation mechanism of individual alumina nanotubes wrapping metal (Cu and Fe) nanowires

Formation Mechanism of Carbon Encapsulated Fe Nanoparticles in the Growth of Single-/Double-walled Carbon Nanotubes

Fabrication and growth mechanism of Ni-filled carbon nanotubes by the catalytic method