Abstract:Subjecting a normal mechanical vibration to a cooling slope plate, is a proposed method for preparing semisolid nondendritic slurry, named shear-vibration coupling sub-rapid solidification (SCS). Taking Al-8Si alloy as model material, the temperature field and distribution field of solid or liquid phase during SCS were simulated using COMSOL Multiphysics software to primarily choose the optimal processing parameters. Subsequently, the slurries were prepared with the parameters selected according to the simulation results and the microstructures of the slurries were experimentally investigated. Results indicate that the simulation results could provide a basis for roughly choosing the processing parameters, although the calculated solid fractions are always higher than the experimental ones. The processing parameters affect the primary grain size, shape factor and solid fraction mainly through altering the contact duration of melt on the plate, and thus affecting the cooling effect on the melt, nucleation rate, and grain dissociation and proliferation. Experiments with optimized processing parameters show that the primary grains in the slurry have an average size of about 32 µm and shape factor of 1.38, and are quite uniform, even at the highest pouring rate of 2.81 kg·s-1, the size and shape factor are about 46 µm and 1.7, respectively, which implies that the proposed SCS is a promising technology for efficient fabrication of high-quality Al slurry available for engineering applications.

Preparation of Semi-solid A356 Aluminum Alloy Slurry by TBR (Taper Barrel Rheomoulding) Technology

Preparation of Semi-Solid A356 Al Alloy Slurry by Repeated Heating-Cooling Method with Elliptical-Twisted Tubes

Microstructural Features of Semi-Solid A357 Alloy Slurry Under High-Shear Melt Processing

Preparation of A356 aluminum alloy semi-solid slurry by damper cooling tube method

New technique for preparing A356 alloy semisolid slurry and its rheo-diecast microstructure and properties

Influences of Master Alloys and Their Preparation Conditions on Microstructures of Semi-solid A356 Alloy Slurries

On-line Preparation Technology of Semi-Solid Slurry of A356.2 Alloy

Performance of semi-solid slurry produced by twin-screw stirring mixer and rheo-diecasting process of AZ91D alloy

Effects of Solid–Liquid Mixing on Microstructure of Semi-Solid A356 Aluminum Alloy

A356 aluminum alloy semisolid slurry prepared by damper cooling tube process

Preparation of semisolid A356 alloy by a cooling slope processing

Preparation and Rheocasting of Semi-solid Aluminum-alloy Slurry with Indirect Ultrasonic Vibration Process

Rapid Multiple Slurry-Preparation Technology of Melt Treatment and Reversible Electromagnetic Stirring

Efficient fabrication of semisolid nondendritic Al alloy slurry with high quality

Development of Non-Dendritic Microstructure of Aluminum Alloy in Semi-Solid State under Ultrasonic Vibration

Development of Microstructure of Semi-Solid A356 Alloy by Alternating Electromagnetic Stirring

Effects of Pouring Temperature on Solidification Behavior of Aluminum Alloy Melt with Electromagnetic Stirring

Preparation and Rheocasting of Semisolid Slurry of 5083 Al Alloy with Indirect Ultrasonic Vibration Process

An investigation on semi-solid forming of A360 aluminium alloy by mechanical stirring

Microstructure, Properties, and Numerical Simulation of Semi-Solid Aluminum Alloy under Planetary Stirring Process

Comparison Between Two Rheocasting Processes of Damper Cooling Tube Method and Low Superheat Casting