Abstract:Graphene-thermopolyurethane (G-TPU) composite films were fabricated and the effects of the TPU initial concentration, characteristics of TPU, and graphene loading on the electrical, mechanical, thermal, infrared thermal response and near-infrared-light-assisted self-healing properties of the composite films were investigated in detail. The experimental results demonstrate that the comprehensive performances of the composite film are related to the initial concentration of the TPU solution and the characteristics of the TPU and the graphene loading. The composite film prepared from TPU solution with low initial concentration can have conductivity under the condition of low graphene content. However, the composite film prepared with appropriate initial concentration of TPU solution and high graphene loading is conducive to obtain high conductivity. After 60 s of near-infrared illumination, the temperature of the composite film first increases and then decreases with the increase in graphene loading until it reaches saturation. The near-infrared light thermal response of the composite film with high graphene loading is related to the initial concentration of TPU solution, while the near-IR thermal response of the composite film with low graphene loading is independent of the initial concentration of TPU. The surface micro-cracks of the composite film almost disappeared after 10 min of near-infrared illumination. The resistance of the conductive composite film increases after healed. The composite film prepared with low melting point TPU is more favorable to obtain high near-IR thermal self-healing efficiency.

Preparation and Piezoresistive Properties Study of Conductive Graphene/Thermoplastic Polyurethane Composites

Preparation of Functionalized Graphene/thermal Conductive Polyurethane Films

Preparation of polyester/reduced graphene oxide composites via in situ melt polycondensation and simultaneous thermo-reduction of graphene oxide

An Infiltration Method to Synthesize Thermoplastic Polyurethane Composites Based on Size-Controlled Graphene Foams

Preparation and Properties of Modified Graphene Oxide/Polyurethane Composites

Influence of Characteristics of Thermoplastic Polyurethane on Graphene-Thermoplastic Polyurethane Composite Film

Combustion Behavior and Thermal Stability of TPU Composites Based on Layered Yttrium Hydroxides and Graphene Oxide

High Loss Factor Piezoelectric Damping Composite with Three-Dimensional Reduced Graphene Oxide As the Conductive Phase

Facile fabrication of polyurethane-based graphene foam/lead zirconate titanate/polydimethylsiloxane composites with good damping performance

Thermal Conductivities of PU Composites with Graphene Aerogels Reduced by Different Methods

Preparation and PTC properties of multilayer graphene/CB/HDPE conductive composites with different cross-linking systems

Strong and Conductive Polybenzimidazole Composites with High Graphene Contents

Effects of treatment temperature on the reduction of GO under alkaline solution during the preparation of graphene/geopolymer composites

In Situ Polymerization of Graphene Nanosheets and Polyurethane with Enhanced Mechanical and Thermal Properties

Testing the influence of the temperature, RH and filler type and content on the Universal Power Law for new reduced graphene oxide TPU composites

In Situ Polymerization Preparation and Mechanical Properties of Nanocomposites Based on PA10T/10I-block-PEG Copolymer and Graphene Oxide

Actuation behavior of PDMS dielectric elastomer composites containing optimized graphene oxide

Preparation and properties of silanized functionalized graphene/polyurethane composites

Communication—Enhanced Dielectric Constant of Polymer Composites Via Regulating Thermal Reduction Treatment Time of Graphene Oxide

Near-Infrared-Light-Assisted Self-Healing Graphene-Thermopolyurethane Composite Films

High‐performance epoxy composites improved by uniformly dispersed and partly thermal reduced graphene oxide sheets