Biphasic calcium phosphate nanocomposite loaded with bone marrow stromal cells for repair of critical cranial defect in rats
Tao Wang,Wei-dong Tian,Sheng-wei Li,Yun-mao Liao
DOI: https://doi.org/10.3321/j.issn:1673-8225.2008.14.003
2008-01-01
Abstract:Background: Traditional bioceramics materials, as the carrier for tissue engineering, have been limited to certain application due to their unsatisfactory performances, such as great fragility, difficult shaping process and in vivo degradation, which will affect the new bone formation and later reconstruction. Objective: To observe the osteogenesis ability of biphasic calcium phosphate nanocomposite (NanoBCP) served as tissue engineered carrier for repairing cranial defect. Design, time and setting: The animal controlled experiment was carried out according to random grouping in the Key Laboratory of Oral Biomedical Engineering, Ministry of Education, Sichuan University from September 2004 to May 2005. Materials: Forty-eight male SD rats, two months old and weighing 180-200 g, were prepared into critical-size defect models in the full-thickness cranial bone. The porosity of NanoBCP scaffold was 60%-80% and the pore size was 100-400 χ m. Both NanoBCP and autogenous bone marrow stromal cells (BMSCs) were offered by the Key Laboratory of Oral Biomedical Engineering, Ministry of Education, Sichuan University. Methods: All rat models were randomly divided into three groups, and each group contained 16 animals. In NanoBCP/BMSCs group, BMSCs were cultured in inducing liquid containing dexamethasone, antiscorbic acid and β -sodium glycerophosphate, then the defects were filled with the NanoBCP/BMSCs composites; In pure NanoBCP group, the defects were filled only with NanoBCP; and blank control rats were filled with nothing. Main outcome measures: At 4, 16 and 24 weeks after implantation, the osteogenesis activity was evaluated by radiographic analysis, gross observation and histological examination. Results: All of 48 SD rats were involved in the result analysis. 1 At 4 and 16 weeks postoperatively, more newly formed bone was found in NanoBCP/BMSCs group, and they were positive for type I collagen immunohistochemical staining. At 24 weeks, cranial defects were completely healed in NanoBCP/BMSCs group, and partly healed in pure NanoBCP group. Blank controls showed no detectable signal of bone defect repair. 2 At 4 and 24 weeks postoperatively, the density of shadow image in cranial defect areas was increased gradually in NanoBCP/BMSCs group, and newly formed bone was close to normal bone; In pure NanoBCP group, the ring low-density was presented in cranial defects and increased along the periphery of the skull, the central domain showed uneven density image. Conclusion: The NanoBCP/BMSCs composites can repair cranial defects effectively.