Property study of Ba0.2Sr0.8La4Ti4O15 microwave dielectric ceramics prepared by two-step sintering

Ya WANG,Shuren ZHANG,Xiaohua ZHOU
2013-01-01
Abstract:Ba0.2Sr0.8La4Ti4O15 microwave dielectric ceramics were prepared using a two-step sintering method,and compared with the samples prepared using the conventional single-step sintering method by characterizing the crystal phase,microstructure and microwave dielectric properties of the ceramics.The results indicate that the Ba0.2Sr0.8La4Ti4O15 ceramics prepared by two-step sintering is composed of fine grains with uniform size,caused by long term temperature maintaining,and shows no crack and better dielectric properties in comparison to the samples prepared by single-step sintering.When the first-step sintering temperature is 1 600 ℃ and the second-step sintering temperature is 1 500 ℃ and maintained for 10 h,the prepared ceramics sample shows the best dielectric performance: εr = 46.5,Q?f = 65 496 GHz,τf = –12.1×10–6 /℃.