Abstract:Ethylenediamine-doped (EDA-doped) polyaniline (PANI) films were deposited via spin coating technique on a glass substrate. The samples were annealed at different times and temperatures. The characterizations of the prepared PANI films were described by X-ray diffraction (XRD), transmission electron microscopy (TEM), and Fourier transform infrared spectroscopy (FT-IR). It is found that the conductivity changes under deep mouth exhaling for 150/1 h sample is 1.65 times faster than the films annealed at 100°C/4 h. The response and recovery time of the 150/1 h EDA-doped PANI film is decreased by order of 0.63 and 1.29 s than those films dried at 100°C for 4 h, respectively. The 150/1 h EDA doped PANI film during deep exhaling its conductivity increased abruptly from 2.2 × 10 –7 to 0.026 S/cm –1 . In a few seconds, following an inhalation, there occurs a complete transition to the dry state conductivity. Furthermore, the increment in conductivity of the EDA-doped PANI films was determined at various RH levels (20, 40, 60, 80, and 90%) with exposure and evacuation of the humid air. The doped PANI sample annealed at 150°C for 1 h exhibit the highest conductivity at 90% RH. The conductivity was increased from 2.16 × 10 –7 S/cm for the insulating state at the dry state to 0.23 S/cm for the semiconducting state at 90% RH. Consequently, the 150/1 h sample showed an increase in conductivity by order of 10 6 at 90% RH. For all samples, the conductivity progressively rises as the RH value increases till 90% of RH value samples exhibit an abrupt increase in conductivity except the 100°C/4 h sample. The highest conductivity is 0.041 S/cm at 90% RH obtained for the case of 150/30 min sample, whereas the 150/1 min and 100/4 h films show maximum conductivity of 0.027 and 0.007, respectively.

Annealing Effects of Dilute Polyaniline/NMP Solution

Preparation of Polyaniline Doped with Acid and Polymer Using Electrochemical Deposition

Fabrication of one dimensional polyaniline nanofibers by UV-assisted polymerization in the aqueous phase.

Preparation and Characterization of Polyaniline/Mmt Conductive Composites

A Very Thin Layer of NiO, Ni(OH)2 Nanosheets Arrays with Organic Functional Modification of Polyaniline

Raman spectroscopic study on the structural changes of polyaniline during heating and cooling processes

Ab Initio Studies of the Differences in the Chemical Reactivity and Electronic Properties of Polyaniline and Its Derivatives

Wet Chemical Synthesis of Entangled Nano-fibrous Conducting Polyaniline (PANI) Mesh: Effect of Heating and Stirring

Liquid Crystalline Assembiles from Selp-Doped Polyaniline

Synthesis of Polyaniline/mcm‐41 Composite Through Surface Polymerization of Aniline

Polyaniline plasticized with 1-methyl-2-pyrrolidone: structure and doping behavior

A Study on the Synthesis, Characterization and Properties of Polyaniline Using Acrylic Acid As a Primary Dopant. I: Polymerization and Polymer

Electrical and Structural Analysis of Conductive Polyaniline/polyacrylonitrile Composites

Tailoring physical properties and electrochemical performance of polyaniline thin films via chemical bath deposition

Functionalization-Induced Changes In The Structural And Physical Properties Of Amorphous Polyaniline: A First-Principles And Molecular Dynamics Study

Polyaniline Morphology and Detectable Intermediate Aggregates

Synthesis and Properties of Polyaniline Nanostructures Using Different Ferric Salts

Mechanistic study on the growth of Sn-doped polyaniline synthesized by one-step electropolymerization

Enhanced adsorption of cationic and anionic dyes from aqueous solutions by polyacid doped polyaniline

Investigation of Insulator-to-Semiconductor Fast Transition in Sheet-Like Polyaniline Films

Interfacial polymerized copolymers of aniline and phenylenediamine with tunable magnetoresistance and negative permittivity