Research on the properties of modified indanthrene blue thin polarizing films

GONG Jian-xun,LIU Zheng-yi,ZENG De-chang,WEN Li-shi

DOI: https://doi.org/10.3969/j.issn.1004-244X.2007.05.005

2007-01-01

Abstract:Thin-film polarizers are favorable for the miniaturization, integration and light-weight of liquid crystal display devices. Sulfonic acid groups were introduced by modified process. The polarized light analysis of modified indanthrene blue RSN aqueous solution showed that their molecules were self-assembled lyotropic liquid crystal phases with strip textures. The polarizing efficiency of thin coating films in 600～730 nm visible light wavelength reaches above 80% and meets the practical requirements with the thickness of 0.4～1.2 μm. The scratch left on the surface showed high bond strength between thin films and the substrates. UV-Vis spectrometer indicated that the transmittance fell down and the polarizing efficiency kept constant after stabilization process. The analysis of surface morphology indicated that the generation of micro-cracks on surface was the main cause to make the transmittance decrease. The polarizing efficiency of thin films and the polarization properties of visible light wavelength were improved with the thickness growing, but the transmittance fell down. The results of experiments proved that modified indanthrene blue RSN thin polarizing films were characterized with good properties of heat and moist heat resistance.