Synergetic Contributions in Phase Boundary Engineering to the Piezoelectricity of Potassium Sodium Niobate Lead-Free Piezoceramics
Xiang Lv,Junwei Zhang,Yao Liu,Fei Li,Xi-xiang Zhang,Jiagang Wu
DOI: https://doi.org/10.1021/acsami.0c12424
2020-08-04
Abstract:Although the pronounced piezoelectricity was obtained in (K, Na)NbO<sub>3</sub> piezoceramics with the phase boundary engineering (PBE), the physical mechanisms remain pending. Here, we revealed for the first time how PBE influences the piezoelectric properties through synergetic contributions. Cryogenic experiments confirm that PBE constructs a phase coexistence, consisting of rhombohedral (R), orthorhombic (O), and tetragonal (T) phases, with a structural softening, by which a high piezoelectric coefficient <i>d</i><sub>33</sub> of 555 pC/N and the enhanced temperature stability of strain are achieved. The phenomenological theory and transmission electron microscopy demonstrate that the superior <i>d</i><sub>33</sub> hinges on the flattened Gibbs free energy and the abundant nanodomains (10–80 nm), which induce the enhanced permittivity and the coexisting single domain and multidomain zones, respectively. In particular, we disclosed a trade-off relationship between ferroelectric domains and polar nanoregions (PNRs) and found the "double-edged sword" role of PNRs in the piezoelectricity enhancement. Therefore, this work helps understand the physical mechanisms of the piezoelectricity enhancement, benefiting the future research of lead-free piezoceramics.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c12424?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c12424</a>.Preparation process of KNNS-<i>x</i>BAZ-Fe ceramics; related measurements for KNNS-<i>x</i>BAZ-Fe ceramics; room-temperature XRD patterns; temperature-dependent dielectric properties; phase diagram; room-temperature Raman spectra; Rietveld structural refinements; structural softening analysis for samples with <i>x</i> = 0; ε<sub>r</sub>–<i>T</i> (25–400 °C) curves; <i>P</i>–<i>E</i> loops, bipolar strain curves, and unipolar strain curves; temperature-dependent ε′, <i>S</i><sub>neg</sub>, <i>S</i><sub>pol</sub>, and <i>S</i><sub>uni</sub>; domain structure of unpoled samples with <i>x</i> = 0; high-resolution transmission electron microscopy images of samples with <i>x</i> = 0.04; impedance and phase angle of poled samples (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c12424/suppl_file/am0c12424_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology