Abstract:Vertically aligned Pd nanoneedles (NNs) with high aspect ratio and uniform growth density were fabricated on indium tin oxide (ITO) substrates by a facile electrodeposition method, which consisted of a short nanoseed-generating step followed by a growth step. The obtained Pd NNs have a full width at half-maximum (fwhm) of 22 +/- 8 nm and taper angle of 15 +/- 4 degrees X-ray diffraction (XRD) and high-resolution transmission electron microscopic (HRTEM) results imply that the NNs were built through the stacking of {111} facets. The factors influencing the electrochemical nucleation and growth of Pd NNs were systematically studied. It was found that the transient nucleation step at a highly negative overpotential is prerequisite to the formation of the uniformly dispersed and vertically aligned Pd NNs. The morphology, size, and aspect ratio of Pd nanocrystals (NCs) were extremely sensitive to the potential applied in the growth step. High aspect ratio and well-aligned Pd NNs could only be obtained in a narrow potential range from 0.100 to 0.200 V. Bromide ions played a dominant role in shaping the morphology of Pd NCs, while citrate ions acted as an assistant shape-controlling agent. A concentration-gradient-induced growth mechanism of Pd NNs was proposed on the basis of the time-dependent scanning electron microscopic (SEM) results. The formation of a uniform diffusion layer at the Pd NNs/solution interface and the concentration gradient of the precursor within the diffusion layer were responsible for the vertically oriented growth of Pd NNs. The Pd NNs exhibited good surface-enhanced Raman scattering (SERS) activity under the excitation of 488 nm laser, implying its potential application as a SEAS substrate. The SEAS activity of Pd NNs was attributed to the unique morphology and the perpendicular alignment of Pd NNs.

Electrochemical Fabrication of Two-Dimensional Palladium Nanostructures As Substrates for Surface Enhanced Raman Scattering.

Electrodeposition of Vertically Aligned Palladium Nanoneedles and Their Application as Active Substrates for Surface-Enhanced Raman Scattering

Electrochemical Synthesis of Nanostructured Palladium of Different Morphology Directly on Gold Substrate through a Cyclic Deposition/Dissolution Route

Palladium Crystals of Various Morphologies for Sers Enhancement

Tailoring the Edge Sites of 2D Pd Nanostructures with Different Fractal Dimensions for Enhanced Electrocatalytic Performance.

2D surface induced self assembly of Pd nanocrystals into nanostrings for enhanced formic acid electrooxidation

Electrochemically Roughened Palladium Electrodes for Surface-Enhanced Raman Spectroscopy : Methodology, Mechanism, and Application

Electrochemical Growth of Two-Dimensional Gold Nanostructures on a Thin Polypyrrole Film Modified ITO Electrode.

Enhanced Raman scattering on two-dimensional palladium diselenide

Facile Preparation of Dendritic Ag–Pd Bimetallic Nanostructures on the Surface of Cu Foil for Application As a SERS-substrate

Surface-enhanced Raman Scattering from Pure Massive Palladium Electrode Surfaces

Controlled Fabrication of Surface-Enhanced-Raman Scattering-Active Silver Nanostructures on Polypyrrole Films

Kinetically controlled synthesis of triangular and hexagonal nanoplates of palladium and their SPR/SERS properties.

Direct solution synthesis of Pd nanowire networks and their application in surface-enhanced Raman scattering.

Palladium-Coated Gold Nanoparticles with a Controlled Shell Thickness Used as Surface-Enhanced Raman Scattering Substrate

Synthesis and Characterization of Dendritic and Porous Ag–Pd Alloy Nanostructures

Flower-shaped PdI2nanomaterials with Remarkable Surface-Enhanced Raman Scattering Activity

High Performance Surface-Enhanced Raman Scattering Substrate Combining Low Dimensional and Hierarchical Nanostructures

Shape-controlled synthesis and application in surface-enhanced Raman scattering of novel palladium nanoparticles

Shaping Surface of Palladium Nanospheres Through the Control of Reaction Parameters.

Synthesis of Au@Pd core–shell nanoparticles with controllable size and their application in surface-enhanced Raman spectroscopy