Study on Vapor-Phase Beckmann Rearrangement of Cyclohexanone Oxime over B_2O_3/TiO_2-ZrO_2 Catalyst I. Effect of B_2O_3 Loading
DS Mao,GZ Lu,QL Chen,ZK Xie,YX Zhang
DOI: https://doi.org/10.3321/j.issn:0253-9837.2002.01.003
IF: 16.5
2002-01-01
Chinese Journal of Catalysis
Abstract:A series of B2O3/TiO2-ZrO2 solid acid catalysts with B2O3 loadings of 0similar to20% were prepared. The catalyst structure, BET surface area, pore size distribution, and acidity were characterized by XRD, FT-IR, N-2-adsorption, and NH3-TPD. The results revealed that when the boria loading less than or equal to5%, the catalysts remained amorphous after calcination at 600degreesC and the boron atoms in the catalysts was present mainly in tetrahedral BO4 units. When the B2O3 loading greater than or equal to8%, TiO2-ZrO2 in the catalysts existed in ZrTiO4 phase and B2O3 existed mainly as vitreous glass, which was constructed mainly by trigonal BO3 units. As the B2O3 loading increased, the surface area of the catalysts decreased and the pore size became larger. The catalytic properties of the B2O3/TiO2ZrO2 catalysts for Beckmann rearrangement of cyclohexanone oxime to c-caprolactam were investigated at 300degreesC. It was found that the caprolactam selectivity increased with increasing B2O3 loading, but the caprolactam yield showed a maximum at 12% boria loading. It is proposed that the caprolactam selectivity of the B2O3/TiO2ZrO2 catalyst is closely correlated with its acid strength distribution and pore size.