The Texture,Structure and Surface Acidity of B_2O_3/ZrO_2 Solid Acid Catalyst Calcined at 700℃
LI Wen-sheng,YIN Shuang-feng,DAI Wei-li,XU Bo-qing,ZHOU Xiao-ping
DOI: https://doi.org/10.3969/j.issn.1001-3555.2007.04.005
2007-01-01
Abstract:The effects of boria loading(0%~19.3%) on the texture, structure and surface acidity of B2O3/ZrO2 catalysts calcined at 700 ℃ were studied by BET、 XRD、 FT-IR、 XPS、 FT-Raman and NH3-TPD techniques.The surface area of the B2O3/ZrO2 increases with the boria content,and then decreases after the boria content exceeds 4.1%.The percentage of tetragonal zirconia increases with increasing of boria loading,and reaches a maximum value at B2O3 loading of 11.7%;further increase of B2O3 results in the decline of the percentage.The change of the crystal size of tetragonal ZrO2 vs.B2O3 loading is opposite to the trend of the percentage of tetragonal ZrO2 vs.B2O3 loading.The boria on the ZrO2 support is mainly composed of BO3 structure units.The atomic ratio of B/Zr on the surface of B2O3/ZrO2 catalyst increases with the increment of boria loading.The numbers of total acid sites,weakly acidic sites,intermediate strong acid sites and strong acid sites become large with the boria loading,and a maximum values appears at 8.3% B2O3 loading.However,the percentage of the intermediate strong acid sites increases with the increment of the boria content,following the same trend as the atomic ratio of B/Zr on the surface with boria loading,suggesting that the BO3 structure units is mainly responsible for the formation of intermediate strong acid sites.The correlation between the surface acidity and catalytic performance of B2O3/ZrO2 catalyst discloses that the intermediate strong acid sites are active for catalyzing the gas-phase Beckmann rearrangement of cyclohexanone oxime into caprolactam.