Abstract:TiC–TiB2 composite cermet tool materials were fabricated by the hot pressing process in vacuum at 1450°C for 30min under 32MPa. The mechanical properties at ambient temperature, the high temperature flexural strength and the high temperature fracture toughness were tested in air. The content of Ni–Mo had significant influence on the microstructure and mechanical properties of the composites at ambient temperature. TBNM8 (TiC+TiB2+8wt%Ni–Mo) had the optimum comprehensive mechanical properties at ambient temperature with flexural strength of 921.2±140MPa, fracture toughness of 7.18±0.5MPa·m1/2 and Vickers hardness of 22.4±1.0GPa. The great mechanical properties of TBNM8 were ascribed to its fine and homogeneous microstructure as well as the mixed mode of intergranular and transgranular fracture. This paper focused on the investigation of the flexural strength and the fracture toughness increment/degradation mechanisms of the materials at elevated temperatures. The flexural strength of TBNM8 decreased gradually with increasing temperature. The strength degradation was ascribed to the softening of grain boundary, the surface oxidation and the elastic modulus degradation. The improvement of the fracture toughness of TBNM8 at 900°C was attributed to the grain boundary sliding which resulted in plastic deformation. But the fracture toughness of TBNM8 at 1000°C decreased due to the serious oxidation of TiC and TiB2.

Multiwalled Carbon Nanotubes–TiB2–Ni Composite: Microstructure and Mechanical Properties

Microstructure and Properties of In-Situ TiC Reinforced Copper Nanocomposites Fabricated Via Long-Term Ball Milling and Hot Pressing

Effect of TiB_2 content on microstructure and mechanical properties of in-situ fabricated TiB_2/B_4C composites

Preparation and Properties of Titanium Diboride Ceramic Matrix Reinforced by Carbon Nanotubes

Processing of Multi-Walled Carbon Nanotube-Reinforced Tini Composites by Hot Pressed Sintering

Microstructure and Mechanical Properties of Cu Matrix Composites Reinforced by TiB2/TiN Ceramic Reinforcements

Preparation and elevated temperature compressive properties of multi-walled carbon nanotube reinforced Ti composites

CNTs/Cu-Ti Composites Fabrication Through the Synergistic Reinforcement of CNTs and in Situ Generated Nano-Tic Particles

A Novel Microstructure and Its Effects on Mechanical Properties of TiC/TiB_2/MoSi_2 Composites

Rapid in-situ reaction synthesis of novel TiC and carbon nanotubes reinforced titanium matrix composites

Sintering And Enhanced Mechanical Properties Of Densified Multiwalled Carbon Nanotube/Tin Composites

Microstructural Evolution and Mechanical Properties of Carbon Nanotubes–reinforced TZM Composites Synthesized by Powder Metallurgy

Microstructure and Mechanical Properties of TiC–TiB2 Composite Cermet Tool Materials at Ambient and Elevated Temperature

Effects of the addition of multi-walled carbon nanotubes on the microstructure and properties of Ti(C,N)-based cermets prepared by spark plasma sintering

Influence of hot pressing on microstructure and mechanical properties of combustion synthesized TiB2–Cu–Ni composite

Microstructure and Mechanical Properties of TiN–TiB2–hBN Composites Fabricated by Reactive Hot Pressing Using TiN–B Mixture

Thermomechanical Processing of a Near-α Ti Matrix Composite Reinforced by TiBw

Mechanical Properties and Strengthening Effects of in Situ (Tib+tic)/ti-1100 Composite at Elevated Temperatures

The Influence of CNTs on the Microstructure and Ductility of CNT/Mg Composites

Mechanical Properties and Strengthening Mechanisms of in Situ (Tib+tic)/ti-1100 Composite at Elevated Temperature

Optimization of the mechanical properties of CNTs/Cu composite by regulating the size of interfacial TiC