Abstract:Highly dispersed ZnO nanoparticles have been successfully prepared after calcinations of the precursors obtained at room temperature via the chemical reaction of zinc sulfate and sodium carbonate in the presence of cetyltrimethylammonium bromide. The particle size distribution of ZnO nanoparticles varies from 61.5 to 79 nm, exhibiting a highly dispersive and narrow size distribution. The average diameter size is 69.8 nm. The transmission electron microscopy shows that ZnO nanoparticles have a hexangular structure, exhibiting a polycrystalline feature. After a hydrothermal process (120-200 degrees C) for the precursors, hexahedral prismlike nanorods (lengths ranging from 3 to 5 mu m and diameters of 80-300 nm) and hexahedral prismlike nanorods with two sharp tips (lengths of 30-70 mu m and central diameters of 1.5-2.0 mu m) can be synthesized. The photoluminescent spectra reveal that the synthesized ZnO nanoparticles present a weak and broad emission band around 400 nm, whereas hexahedral prismlike nanorods and hexahedral prismlike nanorods with two sharp tips exhibit a strong and narrow emission band at 386 and 384 nm, respectively. All of the synthesized ZnO samples show good photocatalytic reactivity on the decomposition of organic dyes.

Morphology-Controlled Zno Particles from an Ionic Liquid Precursor

Synthesis of Zno Nanoparticles with Controlled Shapes, Sizes, Aggregations, and Surface Complex Compounds for Tuning or Switching the Photoluminescence

Morphology Control Of Cuo Micro-Particles Using Zn2+ Ion And Ultrasonic Treatment

Morphology Investigation of Hydrothermally Prepared ZnO Micro-Crystals Influenced by Cu2+ Ions

Control of ZnO Morhpology by Solution Route

Morphology-Controllable synthesis of ZnO nano-/Micro- Structures by a solvothermal process in ethanol solution

Low-temperature growth of uniform ZnO particles with controllable ellipsoidal morphologies and characteristic luminescence patterns.

One-step, solid-state reaction to ZnO nanoparticles in the presence of ionic liquid

Morphology-controlled Synthesis of Flowerlike ZnO Nano/microstructures and Their Photocatalytic Property.

Morphology control and transition of ZnO nanorod arrays by a simple hydrothermal method

Controllable Morphology of ZnO Nanostructures Via a Solvothermal Route

Preparation and Photoluminescence of ZnO Complex Structures with Controlled Morphology

Controllable fabrication of various ZnO micro/nanostructures from a wire-like Zn–EG–AC precursor via a facile solution-based route

Morphology Controlling and Optical Property of ZnO Prepared by Hydrothermal Method

Zno Microcrystals With Diverse Morphologies

Controlled Synthesis of 1D ZnO Nanostructures Via Hydrothermal Process

Systematic synthesis of ZnO nanostructures.

Morphology-controlled synthesis of ZnO 3D hierarchical structures and their photocatalytic performance

Morphological control of ZnO nanostructures by electrodeposition.

Shape and size control of ZnO nanostructures via a simple solution route.

Controllable Synthesis of Highly Dispersed Zno Nanoparticles and Nanorods