Abstract:Ti-6Al-4V alloy is applied in the production of jet engines and other aeronautical components. The Cr/CrN multilayer coating improves the wear, corrosion and oxidation properties of titanium alloys. However, the influence of hard coatings on fatigue properties needs to be investigated to ensure structural integrity. The present work aims to estimate the fatigue crack nucleation and propagation periods of a Cr/CrN coated Ti-6Al-4V alloy at high-stress and low-stress levels. The material used in this work was the Ti-6Al-4V alloy with an equiaxed microstructure and a yield strength of 1000 MPa. The coating was deposited through the DC sputtering method with 8 bilayers of chromium (Cr) and chromium nitride (CrN), achieving 16 layers and a total thickness of about 5 micrometers. Axial fatigue tests were performed at room temperature for the uncoated and coated titanium alloy. Scanning electron microscopy observation of the fracture surfaces showed that the cracks nucleated at the coating and propagated without deflections to the substrate. The Paris law was applied to estimate the fatigue crack propagation period of the Ti-6Al-4V alloy substrate, considering an initial crack with the size of the coating thickness. The results showed that the crack propagation period for the coated samples represented more than 90% of the fatigue life at the high-stress level of 1000 MPa, while it accounts only for about 1% of the fatigue life at the low-stress level of 700 MPa. The fatigue life debit of the Cr/CrN coated material with 8 bilayers and 5 micrometers can be attributed to the significant crack nucleation period reduction due to the brittle layers of CrN compared to the uncoated Ti-6Al-4V alloy. The detrimental coating effect was more substantial at the high-cycle fatigue regime when the crack nucleation period accounts for the majority of the fatigue life.

Fracture Toughness and Repeated Impact Fatigue Properties of Cr-N Hard Coatings

Mechanical Properties and Fracture Toughness of Multilayer Hard Coatings Using Nanoindentation

Preparation of Cr Hard Coatings by Ion Beam Assisted Electron Beam Vapor Deposition on Ni and Cu Substrates

Evaluation of the Adhesion and Failure Mechanism of the Hard CrN Coatings on Different Substrates

Cr/CrN coating effect on the fatigue crack nucleation period of Ti-6Al-4V alloy

Structure, mechanical and tribological properties of thick CrNx coatings deposited by HiPIMS

Microstructure effects on fracture failure mechanism of CrAl/CrAlN coating

Hardening mechanism and plastic deformation behavior in super-hard AlCrNbSiTiN high-entropy nitride nanocomposite coatings

Effect Of Cu Content And Ion Beam Bombardment On Microstructure And Mechanical Properties Of Cr-Cu-N Films

Mechanical property and cracking mechanism of Cr-coated Zr alloy under tensile and compressive loading

Fatigue and Mechanical Behavior of Ti-6Al-4V Alloy with CrN and TiN Coating Deposited by Magnetic Filtered Cathodic Vacuum Arc Process

Durability of Plasma-Sprayed Cr 3 C 2 -Nicr Coatings under Rolling Contact Conditions

Evaluation of wear resistance of CrN, CrAlN, and TiAlN coatings deposited by multi-arc ion plating on spinning die of Cr12MoV

Microstructural origins of high hardness and toughness in cathodic arc evaporated Cr-Al-N coatings

Characterization and tribological properties of Cr-N films by ion beam enhanced deposition

The Cr/Cr2N Multilayer Coating with High Load-Bearing Capacity and Thermal Shock Resistance

Role of high-speed nanoindentation mapping to assess the structure-performance correlation of HVAF-sprayed Cr3C2-25NiCr coating

Stress-dependent fatigue mechanisms of CrC-NiCr coatings in rolling contact

Exploration of electrodeposited process of Ni-Co-Cr coating and investigation of Cr doping strengthening mechanism by indentation simulation

Enhanced Mechanical Properties of CrN Coatings by Plasma Immersion Ion Implantation and Deposition

Performance in Resistance to Surface Fatigue for Cr 3 C 2 –25%NiCr Coatings by Plasma Spray and CDS Spray