Abstract:Magnetic Fe3O4/P (MMA/DVB)((core))-P (St/(GMA/DVB)((shell)) composite microspheres with core-shell structure were prepared by a two-step method. (1) Preparation of the magnetic cores: First, the magnetic miniemulsion composed of organic ferrofluid droplets dispersed in water was obtained by rapid addition of an oil-based magnetite ferrofluid, with a solid content 60 wt%, into the aqueous solution using DNS-86 (polymerizable surfactant) as surfactant in the condition of ultrasonic emulsification. Then, the copolymerization monomers of methyl mathacrylate (MMA) and divinyl benzene (DVB) were injected directly into the magnetic miniemulsion. Because of their hydrophobic character, once the monomers were added into the emulsion, the methyl mathacrylate (MMA) and divinyl benzene (DVB) would have a high tendency to diffuse inside the organic phase of the ferrofluid droplets to form monomer swelling magnetic miniemulsion, Which were supposed to be the main locus for copolymerization. in succession, the temperature was rapidly increased to 70 degrees C and starting the miniemulsion copolymerization to form uniform magnetic latexes. (2) Preparation of the core/shell hybrid polymeric microspheres: Through varying the feeding amount of styrene (St), glycidyl methacrylate (GMA) and DVB, the core-shell structured microspheres were rationally fabricated by the seed emulsion copolymerization using the above magnetic latex as the core emulsion. This preparation process is convenient and effective. Extensive. characterization by X-ray diffraction (XRD), high resolution transmission electron microscopy (HR-TEM), thermogravimetric analysis (TGA) and vibrating sample magnetometer (VSM) showed that the magnetite content of Fe3O4/P(MMA/DVB) composite microspheres was 84 wt %. The magnetite content of the magnetic composite microspheres with core-shell Structure is varied from 20 wt % to 76 wt % by feeding different amount of monomers. The average diameter of the magnetic seeded microspheres and the core-shell composite microspheres is 150 nm and 350 nm, respectively. The functional epoxy groups on the surface of the core-shell composite microspheres can be further modified to load biomolecules.

A Facile Route to Hollow Superparamagnetic Magnetite/polystyrene Nanocomposite Microspheres Via Inverse Miniemulsion Polymerization

Preparation of Hybrid Polymer Nanocomposite Microparticles by a Nanoparticle Stabilised Dispersion Polymerisation

Preparation and Characterization of Ω-Functionalized Polystyrene–magnetite Nanocomposites

Toward Designer Magnetite/polystyrene Colloidal Composite Microspheres with Controllable Nanostructures and Desirable Surface Functionalities.

A Simple Approach to the Synthesis of Hollow Microspheres with Magnetite/Silica Hybrid Walls

Preparation of Monodispersed Hybrid Nanospheres with High Magnetite Content from Uniform Fe3O4 Clusters

Preparation of Polymer–nanoparticle Composite Beads by a Nanoparticle-Stabilised Suspension Polymerisation

Miniemulsion-based assembly of iron oxide nanoparticles and synthesis of magnetic polymer nanospheres

A Facile Synthesis of Superparamagnetic Hybrid Hollow Nanospheres Based on Monodisperse Nickel–zinc Ferrite/polyethylene Glycol and Their Electromagnetic, Microwave Absorbing Properties

Preparation of magnetic polystyrene latex via the miniemulsion polymerization technique

Preparation of Hollow Polymer Microspheres with Hydrophilic/Hydrophobic Asymmetric Surface and Loading of Magnetic Nano-Particles

Facile Preparation of Superparamagnetic Fe3O4/poly(St-co-MPS)/SiO2 Composite Particles with High Magnetization by Introduction of Silanol Groups.

PREPARATION AND CHARACTERIZATION OF MAGNETIC COMPOSITE MICROSPHERES WITH CORE-SHELL STRUCTURE

In Situ Dispersion of Non-Aqueous Fe3O4 Nanocolloids by Microdroplet Coalescence and Their Use in the Preparation of Magnetic Composite Particles.

Hydrophilic Dual‐responsive Magnetite/pmaa Core/shell Microspheres with High Magnetic Susceptibility and Ph Sensitivity Via Distillation‐precipitation Polymerization

Synthesis of Functional Magnetic Porous SrFe12O19/P(St-DVB-MAA) Microspheres by a Novel Suspension Polymerization

Synthesis and Magnetic Properties of Biocompatible Hybrid Hollow Spheres.

Multi-Functional Thermosensitive Composite Microspheres with High Magnetic Susceptibility Based on Magnetite Colloidal Nanoparticle Clusters

Preparation of PS Magnetic Microspheres Via Suspension Polymerization

PREPARATION AND CHARACTERISTICS OF MAGNETIC POLYSTYRENE MICROSPHERE

Preparation of Magnetic Polymeric Particles Via Inverse Microemulsion Polymerization Process