Abstract:Three dimensional (3D) power ultrasound sources with 20 kHz frequency and 14∼22 μm amplitudes were introduced into the solidification process of AZ91 magnesium alloy, and the acoustic spectra versus temperature were synchronously examined. The measured sound pressure monotonically increased with the rise of both ultrasound dimension and amplitude, whereas the transient cavitation intensity firstly increased to its maximum under 3D ultrasound sources at 18 μm amplitude and then unexpectedly declined if further raising the amplitude to 22 μm. The grain size of primary α-Mg phase which was refined down to 16% of that under static solidification mainly depended on the transient cavitation intensity, indicating that the transient cavitation enhanced the nucleation rate by over two orders of magnitudes and dominated the grain refinement. The dislocation density within α-Mg phase increased owing to the intense vibration under semi-solid state. A more homogeneous distribution of divorced eutectic β-Mg14Al12 phase and a smaller amount of β precipitation were induced due to the grain refinement and suppressed segregation for primary α-Mg phase. The microstructural evolution improved the mechanical properties for AZ91 alloy, where its elongation rate and tensile strength were enhanced by the factors of 2.4 and 1.7, respectively. It is demonstrated that applying 3D ultrasound sources provides an effective approach to modulate solidified microstructures and enhance mechanical performances for magnesium alloy.

Microstructures of Mg–Al Binary Magnesium Alloy Solidified with Ultrasonic Treatment

Influence of ultrasonic treatment on the morphology in Mg17Al12 of Mg-9Al binary magnesium alloy

Influence of High-Intensity Ultrasonic Treatment on the Phase Morphology of a Mg-9.0wt.%Al Binary Alloy

Effect of ultrasonic treatment on solidification structure refinement of Mg-Al binary alloy

Effect of Ultrasonic Treatment on Microstructures of Mg-Ca Binary Alloy

Microstructure and Mechanical Properties of Mg–6Zn–0.5Y Magnesium Alloy Prepared with Ultrasonic Treatment

Ultrasonic Treatment of Magnesium Alloy Melts and Its Effects on Solidification Microstructures

Ultrasonic Solidification Mechanism and Optimized Application Performances of Ternary Mg71.5Zn26.1Y2.4 Alloy

Solidification Structures Of Mg-4al-1si Magnesium Alloy Treated By Ultrasonic Field

Improved Mechanical Performances of Dynamically Solidified Mg97.7Y1.4Al0.9 Alloy by Three Dimensional Ultrasounds

Three Orthogonally Arranged Ultrasounds Modulate Solidification Microstructures and Mechanical Properties for AZ91 Magnesium Alloy

Microstructure Evolution and Mechanical Property of Quaternary Cu-7%Al-4%Ni-2.5%Mn Alloy Solidified Within Ultrasonic Field

Effect of Ultrasonic Vibration on Growth Mechanism of Mg2 Si in Mg-9Al-xSi( X=1,6) Alloy

Ultrasonic Effects on Microstructure Evolution and Mechanical Properties of AZ80 Magnesium Alloy

Effects of Ultrasonic Vibration on Microstructure Evolution and Elevated-Temperature Mechanical Properties of Hot-Extruded Mg-6Al-0.8Zn-2.0Sm Wrought Magnesium Alloys

Ultrasonic Solidification and Microstructural Evolution of Binary Al-12.6%Si Eutectic Alloy

Effect of High-Intensity Ultrasonic on Solidification Structure of Mg-Ca Alloy

Effects of ultrasonic treatment on microstructure and mechanical properties of Mg-6Zn-0.5Y-2Sn alloy

Effect of high-intensity ultrasonic on microstructures and grain refinement of magnesium alloy

Mechanical Properties and Formability of Ultrasonic Treated Twin Roll Casting Magnesium Alloy Sheet

Effects of Ultrasonic Treatment on Microstructures of AZ91 Alloy