Synthesis of Cross-linkable Hole-transporting Materials Based on Diels-Alder Reaction and Their Application in Polymer Light-emitting Diodes
Jian-chao Jia,Wan-qing Cai,Sheng-jian Liu,Fei Huang,Yong Cao
DOI: https://doi.org/10.11777/j.issn1000-3304.2017.17032
2017-01-01
Abstract:One of the most challenging tasks in the fabrication of multilayer polymer light-emitting diodes (PLEDs) by solution process is to avoid the interfacial mixing between different layers. To overcome this challenge, extensive efforts have been made in developing crosslinkable materials for PLEDs. However, considering the unfavorable effects of their harsh crosslinking conditions on device performance, it is still desirable to design crosslinkable materials with moderate cured condition to satisfy the requirements of printing device in large scale in the future. Herein, a crosslinkable conjugated polymer with hole-transporting property, poly[9,9-bis(6-furfuryloxyhexyl)-9H-fluorene-co-4,4'-(4 ''-butyltriphenylamine)] (P1) with furan pendant side chains, and a small molecule crosslinker, N,N'-bis[4-(6-maleimidohexyl)phenyl]-N,N'-di-phenylbenzidine (M1) with maleimide functional group, were developed. Due to the fast Diels-Alder reaction between the maleimide in M1 and the furan group in P1, the blend films of P1 and M1 can be quickly crosslinked in extremely short time, resulting in robust hole transporting layer (HTL) films with good solvent resistance, which can overcome the interface mixing problem in solution processed multilayer PLEDs. Such a moderate cured condition (heated at 150 degrees C for similar to 1 min) can decrease negative effects and the optoelectronic property of the resulting HTL film can be tuned also by changing the ratio of the small molecular crosslinker (5% - 100%; maleimide/furan). The PLEDs, with the structure of ITO/poly(3,4-ethylenedioxythiophene): poly(4-styrenesulfonate) (PEDOT: PSS)/P1 + M1/emmisive layer/Ba/Al, were fabricated to investigate the effects of the crosslinker ratio on device performance. The device study results indicated that the HTLs based on P1 + M1 exhibited excellent hole-transporting/electron blocking properties and can prevent emission quenching caused by PEDOT: PSS in the traditional PEDOT: PSS based PLEDs. When M1 content is below 10%, the device displayed lower V-on, higher B-max and LEmax, and the device with HTL based on P1 + 10% M1 exhibited the best performance with LEmax of 9.0 cd A(-1), B-max of 35681 cd m(-2) and V-on of 3.2 V, with a higher brightness of 5000 cd m(-2). Our results indicated that the Diels-Alder reaction between the maleimide and the furan groups can be used to prepare optoelectronic materials for solution processed multilayer engineering of optoelectronic devices, such as PLEDs, polymer solar cells etc.