Properties of Subwavelength-Core Silicon Optical Fibers
Yucheng Ye,Limin Xiao,Yang Hao
DOI: https://doi.org/10.1109/piers.2016.7734305
2016-01-01
Abstract:Silicon Optical Fibers (SOFs) has attracted considerable interest for a wide range of applications, spanning from mid infrared power delivery, Raman amplification, and broadband supercontinuum generation to functionalized optoelectronic devices, microresonators and nonlinear optics. Subwavelength-core SOFs have been fabricated recently, however, their fascinating properties, which are significantly important for all-fiber SOFs integration and nonlinear applications, have not been investigated in detail. Here we will calculate their properties and discuss mode matching and single-mode conditions. The high refractive index contrast between silicon and silica allows for strong mode confinement. Fig. 1(a) shows the mode field diameter (MFD) of the SOF as a function of the silicon core diameter at 1550 nm. When the silicon core diameter is larger than 450 nm, the MFD decreases slowly with the decrease of the core diameter. However, MFD increases steeply when the core diameter is below 450 nm. For example, the MFD is 467nm when the core diameter is 450 nm, and it increases to 9.68 μm at 175 nm, which well matches the MFD of a traditional single mode fiber (SMF). To be a single mode waveguide, the core diameter of a SOF should be less than 378nm at 1550 nm. The inset picture in Fig. 1(b) shows the intensity pattern of y-polarized mode, and we can find that its intensity distributions in two vertical directions are different (Fig. 1(b)). The elliptical mode profile and the discontinuity of the intensity in Y direction are caused by the large discontinuity of the electrical field along the Y axis, and the profile ellipticity is around 0.7. When the core diameter is 225nm the fractional power inside the core decreases to 4.4%, and light can hardly travel through the core when core diameter is less than 120 nm. Fig. 1(c) shows the intensity profile when the core diameter is 175 nm, it is not Gaussian-like shape, which may make it difficult to achieve a perfect mode matching between subwavelength-core SOFs and SMFs.