Abstract:Stress corrosion cracking susceptibility of X80 pipeline steel was investigated in a simulated soil solution using slow strain rate tensile(SSRT) tests.The simulated soil solution was based on the chemical compositions of alkaline Gansu soil in northwest of China.The tests were conducted at different strain rates.The fracture surfaces and secondary cracks were observed using scanning electron microscopy(SEM).The results showed that strain rates had an important role on SCC of X80 steel in simulated soil solutions.Corrosion and mechanical factors have different influences during the SCC processes at different strain rates,which results in the variety of SCC.There was the highest SCC susceptibility at the strain rate of 1.0×10-6s-1.Combined effect of corrosion and mechanics leads to high SCC susceptibility.When the strain rates were lower than 1.0×10-6s-1,enough long corrosion time results in the corrosion of crack in this strain rate range.The crack propagation is restrained.Thus,slight decrease of SCC susceptibilities occurs.As the strain rates were higher than 1.0×10-6 s-1,SCC susceptibilities were low obviously.In this high strain rates range,the mechanical factors have more effect on SCC than corrosion factors,which mainly lead to mechanical fracture of specimens.

Stress Corrosion Cracking of X-70 Pipeline Steels by Eletropulsing Treatment in Near-Neutral Ph Solution

Study of stress corrosion cracking of X70 pipeline steel in near neutral pH solution

Mechanical and Environmental Influences on Stress Corrosion Cracking of an X-70 Pipeline Steel in Dilute Near-Neutral Ph Solutions

Effect of Applied Potentials on Stress Corrosion Cracking Susceptibility of X80 Pipeline Steel in Simulated Soil Solution

Stress Corrosion Cracking of X-70 Pipeline Steel in Near Neutral Ph Solution Subjected to Constant Load and Cyclic Load Testing

Key Factors of Stress Corrosion Cracking of X70 Pipeline Steel in Simulated Deep-sea Environment: Role of Localized Strain and Stress

Mechanistic Aspect of Stress Corrosion Cracking of X80 Pipeline Steel under Non-Stable Cathodic Polarization

Stress corrosion cracking behavior of X80 pipeline steel under alternating current, Desulfovibrio desulfurican and cathodic protection potential

Stress Corrosion Cracking Behavior of X70 Pipeline Steel in Near-Neutral Ph Solutions at Different Temperatures

Effects of Temperature and Applied Potential on the Stress Corrosion Cracking of X80 Steel in a Xinzhou Simulated Soil Solution

Effect of Strain Rate on Stress Corrosion Cracking of X80 Pipeline Steel

Effect of potentials on stress corrosion cracking of X80 pipeline steel in simulated soil solution

Electrochemical Investigation Of Corrosion Of X80 Steel Under Elastic And Plastic Tensile Stress In Co2 Environment

Improvement mechanism in stress corrosion resistance of the X70 pipeline steel in hydrogen sulfide solution by massive laser shock peening treatment

Effect of Dissolved Oxygen on Stress Corrosion Cracking of X70 Pipeline Steel in Near-Neutral Ph Solution

Effect of Potential on SCC Initiation for Pipeline Steel in Near-Neutral PH Solution

Effect of residual tensile stress on stress corrosion behavior of the base metal of x80 uoe pipe

Effect of Zinc-Rich Coating and Cathodic Protection on Stress Corrosion Cracking of Pipeline Steel

Stress Corrosion Crack Initiation Behavior for the X70 Pipeline Steel Beneath A Disbonded Coating

Microstructural Effects in the Development of Near-Neutral pH Stress Corrosion Cracks in Pipelines

Stress corrosion cracking behavior induced by Sulfate-reducing bacteria and cathodic protection on X80 pipeline steel