Abstract:X80 steel plays a pivotal role in the development of oil and gas pipelines; however, its welded joints, particularly the heat-affected zone (HAZ), are susceptible to stress corrosion cracking (SCC) due to their complex microstructures. This study investigates the SCC initiation mechanisms of X80 steel welded joints under practical pipeline conditions with varying levels of cathodic protection. The SCC behaviors were analyzed through electrochemical measurements, hydrogen permeation tests, and interrupted slow strain rate tensile tests (SSRTs) conducted in a near-neutral pH environment under different potential conditions (OCP, −1.1 VSCE, −1.2 VSCE). These behaviors were influenced by microstructure type, grain size, martensite/austenite (M/A) constituents, and dislocation density. The sub-zones of the weld exhibited differing SCC resistance, with the fine-grain (FG) HAZ, base metal (zone), welded metal (WM) zone, and coarse-grain (CG) HAZ in descending order. In particular, the presence of coarse grains, low dislocation density, and extensive M/A islands collectively increased corrosion susceptibility and SCC sensitivity in the CGHAZ compared to other sub-zones. The SCC initiation mechanisms of the sub-zones within the X80-steel welded joint were primarily anodic dissolution (AD) under open-circuit potential (OCP) condition, shifting to either hydrogen-enhanced local plasticity (HELP) or hydrogen embrittlement (HE) mechanisms at −1.1 VSCE or −1.2 VSCE, respectively.

Effect of residual tensile stress on stress corrosion behavior of the base metal of x80 uoe pipe

Stress corrosion behavior of X80 pipeline steel in natural seawater with different dissolved oxygen

Effects of Temperature and Applied Potential on the Stress Corrosion Cracking of X80 Steel in a Xinzhou Simulated Soil Solution

Effect of SRB and Applied Potential on Stress Corrosion Behavior of X80 Steel in High-pH Soil Simulated Solution

Stress-Corrosion-Cracking Sensitivity of the Sub-Zones in X80 Steel Welded Joints at Different Potentials

Stress corrosion cracking behavior of X80 pipeline steel under alternating current, Desulfovibrio desulfurican and cathodic protection potential

Initiation of Stress Corrosion Cracks in X80 and X100 Pipe Steels in Near-Neutral Ph Environment

Microstructural Effects in the Development of Near-Neutral pH Stress Corrosion Cracks in Pipelines

Improvement mechanism in stress corrosion resistance of the X70 pipeline steel in hydrogen sulfide solution by massive laser shock peening treatment

Welding residual stress analysis of the X80 pipeline: simulation and validation

Effect of tensile stress on the hydrogen adsorption of X70 pipeline steel

Effect of Cyclic Loading on the Relaxation of Residual Stress in the Butt-Weld Joints of Nuclear Reactor Piping

The effect of hydrogen on stress corrosion behavior of X65 steel welded joint in simulated deep sea environment

3D finite element analysis and optimization of welding residual stress in the girth joints of X80 steel pipeline

Stress corrosion cracking behavior induced by Sulfate-reducing bacteria and cathodic protection on X80 pipeline steel

EIS analysis on stress corrosion initiation of pipeline steel under disbonded coating in near-neutral pH simulated soil electrolyte

Research on Stress Corrosion Behavior of X70 Pipeline Steel in H2S Environment

Influence of anion and sulfate-reducing bacteria on the stress corrosion behavior and mechanism of X70 steel in a marine mud environment

Effect of Hydrogen Charging on the Stress Corrosion Cracking Behavior of X70 Steel in Simulated Deep Seawater Environment

Degradation Damage of Stress Corrosion in Epoxy Zinc-Rich Coating/Steel Substrate Systems

Electrochemical and Stress Corrosion Mechanism of Submarine Pipeline in Simulated Seawater in Presence of Different Alternating Current Densities