Abstract:Binary silver chalcogenides (Ag2X, X = S, Se, Te) are a group of intriguing thermoelectric materials. When utilised for thermoelectrics, however, the syntheses of these chalcogenides commonly require energy-intensive, high-temperature melting-annealing processes. Herein, we have developed a general surfactant-free and scalable solution synthesis strategy to nano/micro-particles of binary silver chalcogenides, which requires neither high temperature nor long reaction duration. The chalcogenide particles were spark plasma sintered into pellets with porous structures. By modifying the Ag+/X2- molar ratios in the solution precursors from 2:1 to 2:1.1, the thermoelectric properties of the pellets have been effectively optimised, leading to maximum ZT values of 0.84 at 380 K for Ag2Se, 0.59 at 650 K for Ag2Te and 0.27 at 540 K for Ag2S that are comparable to those of samples fabricated by other synthetic methods, such as melting and annealing. This study provides a general surfactant-free solution approach to binary silver chalcogenide nano/micro-materials with tuneable thermoelectric properties.

Solvothermal Preparation of Silver Chalcogenides Ag2e(E=S,Se,Te)

Synthesis of nanocrystalline lead chalcogenides PbE (E = S, Se, or Te) from alkaline aqueous solutions

Solvothermal syntheses of β-Ag2Se crystals with novel morphologies

Room-Temperature Synthesis of Copper and Silver, Nanocrystalline Chalcogenides in Mixed Solvents

General surfactant-free synthesis of binary silver chalcogenides with tuneable thermoelectric properties

A New Low Temperature One-Step Route to Metal Chalcogenide Semiconductors: PbE, Bi2E3 (E=S, Se, Te)

Synthesis and Characterization of Ternary Chalcogenides Ag8SnE6 (E=S, Se)

Sonochemical synthesis of nanocrystalline lead chalcogenides: PbE (E = S, Se, Te)

A solvothermal synthetic route to CdE (E = S, Se) semiconductor nanocrystalline

Room Temperature Synthesis of Metal Chalcogenides in Ethylenediamine.

Solvothermal Preparation of Sb2Se3 Nanowires

A simple solvothermal route to copper chalcogenides

Preparation and Characterization of Ternary Cu–Sn–E (E=S, Se) Semiconductor Nanocrystallites Via a Solvothermal Element Reaction Route

Low Temperature Route Towards New Materials: Solvothermal Synthesis of Metal Chalcogenides in Ethylenediamine

Electrochemical Preparation of Silver Selenide Films and Nanowires from Aqueous Solutions

Synthesis of Silver Selenide Dendritic Crystals Via Glycothermal Route.

Sonochemical Synthesis of Silver, Copper and Lead Selenides

Sonochemical Synthesis of Nanocrystalline Silver Tellurides Ag2Te and Ag7Te4

Synthesis of SnS2 nanocrystals via a solvothermal process

Formation of Cu2−xSe(en)2 in a Solvothermal Process and Conversion to Nanocrystalline Cu2−xSe

Solvothermal Elemental Direct Reaction to Cde (E = S, Se, Te) Semiconductor Nanorod