Effects of Gd3+ substitution on the structure, photoluminescence, scintillation and thermometric features of Pr3+: Lu2Zr2O7 phosphors
Tian Xie,Chengbin Zhang,Pan Jiang,Ruoshan Lei,Lei Lei,Bingpeng Li,Shiqing Xu
DOI: https://doi.org/10.1111/jace.19276
IF: 4.186
2023-06-20
Journal of the American Ceramic Society
Abstract:In this study, it is shown how the photoluminescence (PL), scintillation and optical thermometric properties are managed via the introduction of Gd3+ ions into Pr3+: Lu2Zr2O7. Raman spectra validate that partial replacement of Lu3+ with Gd3+ can promote the phase transition of Lu2Zr2O7 host from the defective fluorite structure to the ordered pyrochlore one. Upon 289 nm excitation, all the samples emit the 483 (3P0→3H4), 581 (1D2→3H4), 611 (3P0→3H6), 636 (3P0→3F2) and 714 nm (3P0→3F4) emissions from Pr3+ ions, which are enhanced with the addition of Gd3+ ions due to the modification of crystal structure. Dissimilarly, the X‐ray excited luminescence (XEL) spectra consist of a strong emission located at 314 nm from Gd3+ ions (6P7/2→8S7/2), together with the typical emissions from Pr3+ ions, which exhibit different dependences on the Gd3+ concentration. When the luminescence intensity ratio between the 3P0→3H6 (611 nm) and 1D2→3H4 (581 nm) transitions is selected for temperature sensing, Pr3+: (Lu0.75Gd0.25)2Zr2O7 shows the optimal relative sensing sensitivity of 0.78%K−1 at 303 K, which is higher than that of the Gd3+‐free sample. Therefore, the developed Pr3+: (Lu, Gd)2Zr2O7 phosphors have the applicative potential for optical thermometry, X‐ray detection and photodynamic therapy. This article is protected by copyright. All rights reserved
materials science, ceramics