Abstract:A catalyst consists of fine aggregates nanoflowers of alumina as support and uniform coating of silver as active component was fabricated to oxidize carbon monoxide. The alumina nanofibers synthesized via a simple electrochemical method. XRD and FE-SEM analysis showed that the thickness of silver deposit was in the range of subnanometer. Elemental mapping also showed a uniform distribution of silver. Also, BET and EDX tests were performed to measure the specific surface area and elemental composition of the catalyst, respectively. Its catalytic activity was measured, and at GHSV equal to 60000 ml/h.g, the end temperature of the oxidizing reaction was 175°C. By increasing the GHSV to 120,000 ml/h.g, the end temperature of the reaction reached 190°C. The thermal stability of the catalyst was also high, as the specific surface area of the catalyst changed from 87 m2/g to 51 m2/g by increasing the temperature from ambient temperature to 900°C. Due to the high stability of alumina, the structure of the catalyst is always stable. On the other hand, feasibility studies have been given special attention to the advancement of the project. Therefore, for the synthesis of nanocatalyst, available precursors and a simple method have been used, so there will be no problem in the mass production of the catalyst. It is hoped to be able to synthesize nanocatalysts with similar structure and mass production capability for other chemical reactions with this method.

Highly active mesostructured silica hosted silver catalysts for CO oxidation using the one-pot synthesis approach.

Preparation of Highly Active Silica-Supported Au Catalysts for Co Oxidation by A Solution-Based Technique

One-Pot Synthesis of Hexagonal Mesoporous Silica Confined Ni Based Catalysts with Advanced Co2 Methanation Performance

One-pot synthesis of meso-structured Pd-CeOx catalyst for efficient low-temperature CO oxidation under ambient conditions.

One-pot synthesis of hexagonal mesoporous silica confined Ni based catalysts with advanced CO 2 methanation performance

Facile Preparation of Mesoporous MCM-48 Containing Silver Nanoparticles with Fly Ash as Raw Materials for CO Catalytic Oxidation

A facile route to ordered mesoporous-alumina-supported catalysts, and their catalytic activities for CO oxidation.

Ultrafine platinum/iron oxide nanoconjugates confined in silica nanoshells for highly durable catalytic oxidation

Synthesis and Catalytic Properties of Porous Metal Silica Materials Templated and Functionalized by Extended Coordination Cages

Noble Metal Nanoparticles Incorporated Siliceous TUD-1 Mesoporous Nano-Catalyst for Low-Temperature Oxidation of Carbon Monoxide

Facile Preparation of Mesoporous Cu–Sn Solid Solutions As Active Catalysts for CO Oxidation

An Efficient Nanoscale Heterogeneous Catalyst for the Capture and Conversion of Carbon Dioxide at Ambient Pressure

Highly Efficient Nano-octahedral Au/γ-Fe2O3 Catalyst Synthesized by Dealloying Combined with Calcination for Low-Temperature CO Oxidation

Mesoporous Co–Mn Spinel Oxides As Efficient Catalysts for Low Temperature Propane Oxidation

One-pot synthesis of Ag@silicalite-1 using different silver amine complexes and their performance for styrene oxidation

Highly dispersed Co nanoparticles embedded in a carbon matrix as a robust and efficient Fischer–Tropsch synthesis catalyst under harsh conditions

Silica-encapsulated Bimetallic Co–Ni Nanoparticles As Novel Catalysts for Partial Oxidation of Methane to Syngas

Synthesis of ultrastable silver catalyst supported on alumina nanofibers for carbon monoxide combustion

One-Pot Synthesis of Ordered Mesoporous NiSiAl Oxides for Catalyzing CO2 Reforming of CH4

Synthetic Pt-Fe(OH) x catalysts by one-pot method for CO catalytic oxidation

Large-scale Synthesis and Catalytic Activity of Nanoporous Cu–O System Towards CO Oxidation