Abstract:Commercial thixoforming is generally based on conventional aluminum-based casting alloys such as A356 and A357, which provide high fluidity and good castability. However, these alloys do not give such high mechanical properties as the alloys that are conventionally wrought such as Al-Cu-Si-Mg alloys, which generally has wide freezing ranges and tend to be prone to inhomogeneous microstructure and hot tearing. In this paper, one kind of aluminum alloy based on Al-Cu-Si-Mg system was thixoformed under different mechanical conditions. The strain induced melt activated (SIMA) route was used to obtain the semisolid slug for thixoforming. The effect of mechanical conditions on the microstructures and tensile mechanical properties in the T6 condition of the thixoformed aluminum alloy were studied. On proper mechanical condition (the base of component is 15. mm), the thixoformed sample reveals a relatively homogeneous structure among different regions and presents no evidence of macro and microporosities, moreover, the tensile mechanical properties are uniform between the wall and the base. The ultimate tensile strength (376. MPa) is close to the wrought target, and the elongation to fracture (18.7%) is even better, nevertheless, the yield strength (220. MPa) is considerably short of the wrought value. On improper mechanical condition (the base of component is 5. mm), the microstructures are inhomogeneous and inferior with respect to those of the former, and present some microporosities and microcracks. Although, a few cracks were filled by the supplied liquid metal, the mechanical properties are not satisfactory (tensile strength of 346. MPa, yield strength of 216. MPa and elongation to fracture of 11.5%). © 2011 Elsevier Ltd.

Preparation and Thixo-forming Characteristics of Mg-Al-Zn Semi-solid Alloy Billets

Preparation of Mg-Al Series Magnesium Alloy Semi-solid Billets and its Thixo-extrusion Forming

Preparation of semi-solid billet of magnesium alloy and its thixoforming

Microstructure and mechanical properties of AZ61 magnesium alloy parts achieved by thixo-extruding semisolid billets prepared by new SIMA

Preparation and thixoforging of semisolid billet of AZ80 magnesium alloy

Microstructure Evolution of AZ91D Magnesium Alloy Semi-solid Billets Prepared by a New SIMA Method

Preparation of Az91d Magnesium Alloy Semi-Solid Billet by New Strain Induced Melt Activated Method

Preparation of Semi-solid AZ91D Billets by new SIMA Method

Microstructure and Properties of AZ80 Alloy Semisolid Billets Fabricated by New Strain Induced Melt Activated Method

Effect of mechanical conditions on the microstructures and mechanical properties of thixoformed Al-Cu-Si-Mg alloy

Research on Thixoforging Magazine Plate of AZ91D Magnesium Alloy in Semi-Solid State

Research on Thixoforging of Magazime Plate of AZ91D Magnesium Alloy

Microstructures of Semi-Solid AZ91D Magnesium Alloys Billets Prepared by Cold Rolling SIMA Method

Application of Equal Channel Angular Extrusion to Semi-solid Processing of AZ91D Magnesium Alloy

Compound Fabrication Technology of Semi-Solid Billet of Al-Si Alloy Based on SIMA Method

Semi-solid thixoforging of nondendritic AlSi7Mg alloy

Microstructure Evolution and Thixoextrusion of Az91d Magnesium Alloy Produced by Sstt

Microstructure evolution and tensile mechanical properties of thixoformed high performance Al-Zn-Mg-Cu alloy

Effect of compression ratio on microstructure evolution of Mg–10%Al–1%Zn–1%Si alloy prepared by SIMA process

Research on Semi-Solid Isothermal Treatment of AM60 Magnesium Alloy Processed by Severe Plastic Deformation

Numerical Simulation of Thixoforging of an Az91d Magnesium Alloy Magazine Plate and Experimental Validation