Abstract:Silica aerogel is a unique nanomaterial with three-dimensional nano-porous networks. However, the microstructures of aerogels are easily damaged at high temperatures environment, weakening the thermal insulation performance. In this work, we prepared thermally stable SiOC nanospheres and then composited them with aerogel matrix. SiOC nanospheres and aerogel matrix have excellent compatibility. SiOC nanospheres can induce the aerogel matrix forming island microstructures after drying process. The presence of the island microstructure leads to a reduce of the inter-skeleton macropore size, which declines from 4.77 μm to 2 μm. The thermal conductivity decreases from 0.0813 to 0.0646 W/ (m K). The volume shrinkage and density also show a clear downward trend. In order to investigate the impact of high-temperature to thermal insulation performance, the aerogel composites are experienced different high-temperature treatment. The results demonstrate that the island microstructure of aerogel is transformed into a spherical shape after high-temperature treatment. The particle diameter increases from 5 μm to 5.7 μm when treated in 200 °C and 400 °C. Upon 400 °C, the diameter reduces from 5.7 μm to 4.4 μm at 800 °C. The variety in the size of the aerogel skeleton particles results in a reduction in the pore diameters of the interskeleton pores from 8 to 3.8 μm. The thermal conductivity decreases from 0.0667 to 0.0466 W/ (m K) treating below 400 °C and increases to 0.0712 W/ (m K), when heat treatment temperature is 800 °C. The enhancement of thermal insulation performance is attributed to the decline of macropores content between skeletons caused by swelling of aerogel particles. The diameters of macropores between skeletons reduce, which can effectively weaken the influence of gaseous heat transfer. This work provides a reference for the preparation of aerogel composites that can maintain excellent thermal insulation properties in high-temperature environment.

Hydrophobic and thermal insulation properties of silica aerogel/epoxy composite

Studies on Thermal Property of Silica Aerogel/Epoxy Composite

Thermal Conductivity of Silica Aerogel Thermal Insulation Coatings

Regulating the hydrophobicity and pore structure of silica aerogel for thermal insulation under humid and high temperature conditions

Synthesis and Characterization of Silica Aerogel and Its Composite Materials

Mechanical, Thermal and Flammability Properties of Glass Fiber Film/Silica Aerogel Composites

High-temperature microtexture, microstructure evolution, and thermal insulation properties of porous Si3N4/silica aerogel composites produced by impregnation

Microstructure And Thermal Insulation Property Of Silica Composite Aerogel

Synthesis and Heat Insulation Performance of Glass Fiber Reinforced SiO2 Aerogel Composites

Transparent, robust, and machinable hybrid silica aerogel with a “rigid-flexible” combined structure for thermal insulation, oil/water separation, and self-cleaning

Rapid Synthesis of Super Insulation Silica Aerogel Composites Strengthened with Mullite Fibers

Facile Construction of the Aerogel/geopolymer Composite with Ultra-Low Thermal Conductivity and High Mechanical Performance

A Novel Silica Aerogel/porous Si3N4 Composite Prepared by Freeze Casting and Sol-Gel Impregnation with High-Performance Thermal Insulation and Wave-Transparent

Investigation of High Temperature Thermal Insulation Performance of Fiber-Reinforced Silica Aerogel Composites

Heat transfer mechanism of TiO 2 -doped silica aerogel

SiOC nanospheres reinforced silica aerogel with excellent compatibility and excellent thermal insulation under high temperature conditions

A silica aerogel-based thermal insulation composite film for metal surfaces in gas industries

Facile Synthesis of Flexible and Hydrophobic Polymethylsilsesquioxane Based Silica Aerogel Via the Co-Precursor Method and Ambient Pressure Drying Technique

Thermal Insulation Performance of Monolithic Silica Aerogel with Gas Permeation Effect at Pressure Gradients and Large Temperature Differences

Microstructure and Properties of the Si3N4/silica Aerogel Composites Fabricated by the Sol–gel Method Via Ambient Pressure Drying

Ambient Pressure Drying as an Advanced Approach to the Synthesis of Silica Aerogel Composite for Building Thermal Insulation