Enhanced hydrogen storage performance of magnesium hydride catalyzed by medium-entropy alloy CrCoNi nanosheets
Shuai Li,Fuying Wu,Yan Zhang,Ren Zhou,Zichuan Lu,Yiqun Jiang,Ting Bian,Danhong Shang,Liuting Zhang
DOI: https://doi.org/10.1016/j.ijhydene.2023.08.308
IF: 7.2
2023-09-05
International Journal of Hydrogen Energy
Abstract:The sluggish de/hydrogenation kinetics and stable thermodynamics of magnesium hydride (MgH 2 ) are unfavorable for its large-scale application. Herein, the medium-entropy alloy CrCoNi nanosheets were synthesized and remarkably enhanced the low-temperature hydrogen storage performance of MgH 2 . Surprisingly, the initial dehydrogenation temperature of 9 wt% CrCoNi modified MgH 2 was greatly reduced from 325 °C to 195 °C, a drop of 130 °C compared to non-additive MgH 2 . Also, the MgH 2 –CrCoNi composite released 4.84 wt% hydrogen at 300 °C even in 5 min and absorbed 3.19 wt% hydrogen at 100 °C within 30 min (3.2 MPa). The calculated de/rehydrogenation activation energy were reduced by 45 and 55 kJ mol −1 , respectively. Further cyclic kinetics investigation indicates that the 9 wt%-CrCoNi doped MgH 2 still presented good stability after 20 cycles, losing only 0.36 wt% hydrogen capacity. The XRD pattern validated that CrCoNi remained stable during the cyclic reaction process. Besides, the uniformly distributed CrCoNi nanosheets were in tight contact with the MgH 2 surface, providing abundant catalytic active sites and low-energy barrier diffusion channels. Under synergistic catalysis, the H atoms are rapidly absorbed and released across the Mg/MgH 2 interface, resulting in excellent kinetic properties. Briefly, this paper provides new references and inspirations to design efficient polymetallic catalysts for hydrogen storage materials.
energy & fuels,electrochemistry,chemistry, physical