Abstract:The orthogonality test was used to obtain the optimal technology for preparing magnetic nanoparticles coated with covalentlybound biofunctional polyethyleneimine(PEI).We propose PEI-Fe3O4 magnetic nanoparticles as a mediator for hyperthermia in vitro and in vivo.The processing of polyethyleneimine modified Fe3O4 magnetic nanoparticles includes the preparation of magnetic Fe3O4 nanoparticles and then integrating the Polyethyleneimine modified magnetic nanoparticles and Fe3O4.Examination and characterization of the polyethyleneimine modified Fe3O4 magnetic nanoparticles were performed using simple methods.Simple analyses of the factors affecting the preparation of polyethyleneimine modified Fe3O4 magnetic nanoparticles were made,and the optimal technology was obtained after the optimization of these factors by means of a L8(27) orthogonality test.The optimal technological conditions obtained were:use of ammonium chloride to keep the pH in the range of 9.3 ～9.7;the ferric ions must be kept in the ratio Fe2 +/Fe3 +=1:1.75;a polyethyleneimine solution with mass-fractional of 20% should be used;a mechanical stirring at of 1400r/min should be maintained;and the reaction temperature should be held at 85℃.The resulting polyethyleneimine modified Fe3O4 magnetic nanoparticles were characterized using Fourier transform infrared spectroscopy,transmission electron microscope,X-ray diffraction,vibrating sample Magnetometry,and Thermogravimetric Analysis.The results show that the particles have a spinel structure,are superparamagnetic,and have good performance Their diameter is about 9.4nm,their magnetic concentration is 82%,and their magnetization is 61.962emu/g.Further investigation is needed to confirm the nanoparticles effectiveness as a mediator for hyperthermia in vitro and in vivo.

Preparation and characterization of PEG-PEI/Fe_3O_4 nano-magnetic fluid by co-precipitation method

Polyol Synthesis of Superparamagnetic Fe_3O_4 Nanoparticles for Magnetic Resonance Imaging

Fe3O4-DMSA-PEI Magnetic Nanoparticles with Small Particle Size: Preparation and Gene Loading

Preparation and Characterization of Magnetic PLA-PEG/Fe3O4 Composite Microspheres

Preparation and Characterization of Polyethyleneimine Modified Fe3O4 Magnetic Nanoparticles

comprehensive study on the synthesis and paramagnetic properties f PEG-coated Fe 3 O 4 nanoparticles

Synthesis And Characterization Of (Fe3o4/Pva)/Sio2 Magnetic Nano-Compositions With Core-Shell Structure

Absorption Properties of Aqueous Ferrofluid Modified by Polyelthylenemine

Synthesis and Characterization of PEG-modified Polymer Magnetic Micropheres

A comprehensive study on the synthesis and paramagnetic properties of PEG-coated Fe 3 O 4 nanoparticles

Synthesis of Fe3O4 Nanoparticles and Preparation of Magnetic Fluids

Synthesis and Magnetic Properties of PEG-Modified Fe3O4 Nanospheres

Preparation and Characterization of Magnetic PLA–PEG Composite Nanoparticles for Drug Targeting

Fabrication and Characterization of Organic-based Fe_3O_4 Magnetic Fluid

Facile One-Pot Synthesis Of Magnetic Nanoparticles With Controllable Morphology And Size Distribution As Targeted Biocarriers

Preparation and performance of suicide gene-encapsulated polyethylene glyeol-polyethylenimine Fe3O4 nano-magnetic fluid

Preparation And Characterization Of Magnetic Polyethyleneimine-Fe3o4 Nanocomposites

Ph Responsive Behavior of Fe3O4@PDEA-PEGMA Core-Shell Hybrid Magnetic Nanoparticles

Preparation and characterization of Fe3O4 nanoparticles used in intelligent polymer gels and intelligent polymer gels drived by magnetic fields

In Situ Preparation Of Size-Controlled Iron Oxide Nanocrystals Using Double-Hydrophilic Multiarm Hyperbranched Polymers As Nanoreactors And Their Magnetofection In Vitro

Preparation and characterization of magnetic microspheres coated with copolymers of two unsaturated monoesters of poly(ethylene glycol)