NEUTRON DIFFRACTION STUDY OF DEUTERIUM OCCUPANCY OF DEUTERIDE OF LAVES PHASE ALLOY Ti0.68Zr0.32MnCrD3.0

Wu Erdong,Guo Xiumei,Sun Kai
IF: 1.797
2009-01-01
ACTA METALLURGICA SINICA
Abstract:The occurrences of diffuse scattering in the neutron diffraction patterns of the deuterides of Laves phase have frequently been reported,but have not been specifically studied.As the diffuse scattering indicates the formation of short range ordering of D and/or alloy atoms in the phase,we have particularly studied the possible short range ordering of interstitial D atoms in the deuteride of a null matrix Laves phase alloy Ti_(0.68_Zr_(0.32)MnCr by neutron and XRD techniques. The neutron diffraction pattern of the deuteride Ti_(0.68)Zr_(0.32)MnCrD_(3.0) has shown not only the Bragg peaks,but also strong diffuse scattering,whereas the corresponding XRD pattern has only shown the Bragg peaks.These phenomena confirm the formation of short range ordering of interstitial D in the deuteride.The D occupancy and short range ordering of the deuteride were analyzed by the Rietveld refinement and Fourier transformation.The analyses suggest that a fraction of D atoms in the deuteride is randomly and unsaturatedly distributed in certain interstices,and forms a long range ordered structure in the crystal lattice.These interstitial atoms are in four types of the A_2B_2 tetrahedral sites,where the occupancies of the D atoms in the 6h_1 and 12k crystallographic sites are higher than those in the 6h_2 and 241 sites.However,other D atoms in the deuteride have stayed away from the centres of the interstitial sites to different extents,and formed the short range ordered structure.These D atoms keep an average interdistance of 0.243 nm for the nearest neighbours,larger than that of about 0.2 nm for the long range ordered D atoms.The short and long range ordered D atoms together form a cluster network surround the Ti/Zr atoms along the c-axis of the lattice.The phenomenon is likely to be caused by the accumulation of great amount of D atoms in the interstices of the alloy.
What problem does this paper attempt to address?