Abstract:A zeolite/polymer composite hollow fiber (CHF) support is used to investigate the effects of three different silica sources (sodium metasilicate nonahydrate, silica sol and sodium silicate) of the synthesis hydrogel on the properties of zeolite LTA membrane prepared on the outer surface of the support by in situ hydrothermal synthesis at 100°C. The as-synthesized membranes and powders from the synthesis hydrogel are characterized by X-ray diffraction. The morphology and thickness of the membranes are observed by scanning electron microscopy. The separation factor and flux are evaluated by pervaporation (PV) test at 75°C using 90wt.% ethanol aqueous solution. It is difficult to obtain high performance membranes on the CHF support using sodium metasilicate nonahydrate as silica source, while continuous zeolite membranes with high separation factor (>10,000) and flux (>6.4kg/m2h) can be well synthesized using silica sol or sodium silicate as silica source. The reason of these differences is further explored by changing the alkalinity of the synthesis hydrogel (the content of sodium hydroxide). It is found that the crystallization rate of the synthesis hydrogel is a crucial factor to obtain zeolite membranes with high PV performance by static in situ hydrothermal synthesis. The separation performance of the membrane synthesized even using sodium metasilicate nonahydrate as silica source can be greatly improved by dynamic hydrothermal synthesis using rotating autoclaves.

Synthesis of Long-Term Acid-Stable Zeolite Membranes and Their Potential Application to Esterification Reactions

A study on the pervaporation of water–acetic acid mixtures through ZSM-5 zeolite membranes

Zeolite Imidazolate Framework Membranes on Polymeric Substrates Modified with Poly(vinyl Alcohol) and Alginate Composite Hydrogels.

ZSM-5 zeolite membranes prepared from a clear template-free solution

Preparation of zeolite MFI membranes on alumina hollow fibers with high flux for pervaporation

Zeolite Mfi Membranes for Separation of Ethanol/Water Mixture

The preparation of zeolite NaA membranes on the inner surface of hollow fiber supports

Microstructure Manipulation of MFI-type Zeolite Membranes on Hollow Fibers for Ethanol–water Separation

High performance zeolite NaA membranes synthesized on the inner surface of zeolite/PES–PI blend composite hollow fibers

Effects of the synthesis hydrogel on the formation of zeolite LTA membranes

Preparation of high-performance zeolite NaA membranes in clear solution by adding SiO2 into Al2O3 hollow-fiber precursor

Fabrication of B-Oriented MFI Zeolite Membranes by a Printing-Transfer Seed Layer Procedure.

Manipulation of the Surface Microstructure and Its Effects on the Flux of NaA Zeolite Membranes in Pervaporation

Influences of adding organic intermediate layer on membrane formation and properties

Effects of Sodium Ions on the Separation Performance of Pure-Silica MFI Zeolite Membranes

Effects of porogen EDTA on morphology of porous silica support and preparation of MFI zeolite membrane

Preparation of zeolite MFI membranes on defective macroporous alumina supports by a novel wetting–rubbing seeding method: Role of wetting agent

Room-Temperature Synthesis of Zeolite Membranes toward Optimized Microstructure and Enhanced Butane Isomer Separation Performance

A Facile Preparation of High Flux NaA Zeolite Membranes by Direct Secondary Growth of Wet Gel Layer

Induction of Zeolite Membrane Formation by Implanting Zeolite Crystals into the Precursor of Ceramic Supports

Synthesis and Low-Temperature Detemplation of High-Silica Mfi Zeolite Membranes