A non-rare-earth-doped self-activated blue fluorescent material of transparent glass-ceramics containing single-phase NaY(MoO 4 ) 2 : The controllable synthesis, crystallization behavior and luminescent properties
Juxia Tong,Zhiwei Luo,Xinzhu Liu,Haozhang Liang,Xinyu Liu,Pan He,Anxian Lu
DOI: https://doi.org/10.1016/j.jallcom.2023.172179
IF: 6.2
2023-09-24
Journal of Alloys and Compounds
Abstract:The glass with components of 50SiO 2 -20B 2 O 3 -20Na 2 O-6ZnO-3MoO 3 -1Y 2 O 3 (mol%) was synthesized by the melt-quenching method, and the corresponding glass-ceramics were obtained after heat treatment. The crystallization behavior of the glass was characterized by the DSC test. By carefully examining the structure and grain size of the NaY(MoO4) 2 crystals with scheelite structure using XRD and SEM, it can be confirmed that the crystal size steadily increases after increasing the crystallization temperature or extending the crystallization time, which is in the range of 27–45 nm. The transmittance of glass-ceramics somewhat declines compared to the precursor glass, although it remains high (>80 %). Under the excitation of 365 nm, the glass-ceramic shows a broad emission band, which is related to the charge transfer of Mo 6+ →O 2- in the [MoO 4 ] 2- unit. The glass-ceramic is heat-treated at 590 °C for 3 h as the optimal heat treatment schedule, and its CIE chromaticity coordinate is located in the blue-light region, indicating the potential application of the non-rare-earth-doped self-activated light-emitting glass-ceramics containing single-phase NaY(MoO4) 2 in the blue light-emitting field.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering