Abstract:A series of porous carbon spheres with precisely adjustable mesopores (4-16 nm), high specific surface area (SSA, ∼2000 m2 g-1), and submicrometer particle size (∼300 nm) was synthesized through a facile coassembly of diblock polymer micelles with a nontoxic dopamine source and a common postactivation process. The mesopore size can be controlled by the diblock polymer, polystyrene-block-poly(ethylene oxide) (PS-b-PEO) templates, and has an almost linear dependence on the square root of the degree of polymerization of the PS blocks. These advantageous structural properties make the product a promising electrode material for electrochemical capacitors. The electrochemical capacitive performance was studied carefully by using symmetrical cells in a typical organic electrolyte of 1 M tetraethylammonium tetrafluoroborate/acetonitrile (TEA BF4/AN) or in an ionic liquid electrolyte of 1-ethyl-3-methylimidazolium tetrafluoroborate (EMIMBF4), displaying a high specific capacitance of 111 and 170 F g-1 at 1 A g-1, respectively. The impacts of pore size distribution on the capacitance performance were thoroughly investigated. It was revealed that large mesopores and a relatively low ratio of micropores are ideal for realizing high SSA-normalized capacitance. These results provide us with a simple and reliable way to screen future porous carbon materials for electrochemical capacitors and encourage researchers to design porous carbon with high specific surface area, large mesopores, and a moderate proportion of micropores.

Synthesis and Electrochemical Performance of A Laminated Hollow Porous Carbon

Mesoporous Carbon Materials As Electrodes for Electrochemical Double-Layer Capacitor

The Structural Optimization and High Electrochemical Behavior of Porous Carbons by Graphitization in Molten Sodium Metals

Carbon-coated mesoporous NiO nanoparticles as an electrode material for high performance electrochemical capacitors

High Performance All-Solid-state Symmetric Supercapacitor Based on Porous Carbon Made from a Metal-Organic Framework Compound

Synthesis of 3D Hierarchical Porous Carbon As an Electrode Material for Electric Double Layer Capacitors

A Novel Synthesis of Hierarchical Porous Carbons from Interpenetrating Polymer Networks for High Performance Supercapacitor Electrodes

Porous carbon with tailored pore size for electric double layer capacitors application

Synthesis of multi-branched porous carbon nanofibers and their application in electrochemical double-layer capacitors

Synthesis and Electrochemical Performance of Microporous Carbon Using A Zinc(Ii)-Organic Coordination Polymer

Preparation of Porous Doped Carbons and the High Performance in Electrochemical Capacitors

Facile Synthesis of Nitrogen-Containing Porous Carbon As Electrode Materials for Superior-Performance Electrical Double-Layer Capacitors

Water bamboo-derived porous carbons as electrode materials for supercapacitors

Hierarchical Porous Carbon Hollow-Spheres As a High Performance Electrical Double-Layer Capacitor Material

Hierarchical porous carbon applied in electric double layer capacitor

Facile Synthesis of Porous‐Carbon Nanoarchitectures As Advanced and Durable Electrodes for Supercapacitors

Hierarchically Porous Nickel Hydroxide/Mesoporous Carbon Composite Materials for Electrochemical Capacitors

Hierarchical Nanoporous Carbon Templated and Catalyzed by the Bicontinuous Nanoporous Copper for High Performance Electrochemical Capacitors

Activated Porous Carbon Spheres with Customized Mesopores Through Assembly of Diblock Copolymers for Electrochemical Capacitor

Hierarchical porous carbon derived from carboxylated coal-tar pitch for electrical double-layer capacitors

Layered Conductive Polymer-Inorganic Anion Network for High-Performance Ultra-Loading Capacitive Electrodes