Abstract:Waste hydrogenation catalysts are usually listed as hazardous wastes due to their high heavy metal contents. These heavy metals such as molybdenum, vanadium, nickel, and cobalt will affect environment, human health, and wildlife. Moreover, the waste hydrogenation catalysts represent a valuable secondary resource, containing a significant quantity of valuable metals, recycling them will bring economic benefits, alleviate the need for mining investment, and reduce the environmental impact of mining. However, the current process presents many environmental and economic challenges, including sulfur dioxide pollution, more reagent consumption, and complicated operation. As a result, a new method is necessary to alleviate these drawbacks. In this work, a novel calcification roasting-acid leaching method was proposed to recycle the waste catalyst. The calcification roasting process was studied focally and systematically, including thermodynamics, reaction mechanisms, and phase transformation. The behaviors of Mo, V, Ni, and Al in the leaching process were studied, and influence factors, including roasting temperature, calcium additives feeding, acid concentration, leaching temperature, leaching time, liquid-solid ratio, and particle size were explored. Under the optimal conditions, the leaching efficiency for Mo and V reached 98.02 % and 97.28 % respectively. In contrast, there is no Ni and Al in the post-leaching solution, demonstrating excellent leaching ability for Mo and V, and robust leaching selectivity. Moreover, this novel method shows environmentally friendly properties, as it reduces SO 2 generation. From the perspectives of resources, environment, and economy, this novel approach shows a competitive advantage and bright prospect.

Study on the Recycling of Valuable Metals in Spent Al2O3-based Catalyst

New Technique of Comprehensive Utilization of Spent Al 2 O 3 -Based Catalyst

A Novel Process for Comprehensive Utilization of Spent Al_2O_3-based Catalyst

Efficient Recovery of All Valuable Metals from Spent HDS Catalysts: Based on Roasting Mechanisms for Enhanced Selective Leaching and Separation

Cleaner recycling of spent Ni–Mo/γ-Al2O3 catalyst based on mineral phase reconstruction

A Study on Recovering Vanadium and Molybdenum from Spent Catalyst

Alkali extraction of valuable metals from spent Mo–Ni/Al 2 O 3 catalyst

Recovering valuable metals from spent hydrodesulfurization catalyst via blank roasting and alkaline leaching

Efficient and Selective Recovery of Mo and V from Spent Hydrodesulfurization Catalysts Via Oxidation Roasting Followed by Na2CO3 and NaOH Leaching

Economical and efficient recovery of Pd and Al2O3 from spent Pd/Al2O3 catalyst with integrated sodium roasting−reductive leaching process

Recovery Of Palladium And Aluminum From Spent Catalysts By Roasting-Leaching

Towards sustainability: A novel process for recycling vanadium and molybdenum from waste hydrogenation catalysts

Comprehensive Recovery of Vanadium and Molybdenum from Ammonia Leaching Residue of Spent Catalyst

Recovery and Regeneration of Al 2 O 3 with a High Specific Surface Area from Spent Hydrodesulfurization Catalyst CoMo/Al 2 O 3

Tuning of vanadium valence for value-added recycling and utilization of vanadium from spent Selective Catalytic Reduction Catalysts

Recovery of Valuable Metals from Spent LiNixCoyMnzO2 Cathode Material Via Phase Transformation and Stepwise Leaching

Studies on Recovery of Vanadium from Desilication Residue Obtained from Processing of a Spent Catalyst

Stepwise separation and recovery of molybdenum, vanadium, and nickel from spent hydrogenation catalyst

Investigations on the Extraction of Molybdenum and Vanadium from Ammonia Leaching Residue of Spent Catalyst

Recovery of Mo and Ni from spent acrylonitrile catalysts using an oxidation leaching–chemical precipitation technique

A Promising Approach to Recover a Spent SCR Catalyst: Deactivation by Arsenic and Alkaline Metals and Catalyst Regeneration