Abstract:One of the most challenging tasks in the fabrication of multilayer polymer light-emitting diodes (PLEDs) by solution process is to avoid the interfacial mixing between different layers. To overcome this challenge, extensive efforts have been made in developing crosslinkable materials for PLEDs. However, considering the unfavorable effects of their harsh crosslinking conditions on device performance, it is still desirable to design crosslinkable materials with moderate cured condition to satisfy the requirements of printing device in large scale in the future. Herein, a crosslinkable conjugated polymer with hole-transporting property, poly[9,9-bis(6-furfuryloxyhexyl)-9H-fluorene-co-4,4'-(4 ''-butyltriphenylamine)] (P1) with furan pendant side chains, and a small molecule crosslinker, N,N'-bis[4-(6-maleimidohexyl)phenyl]-N,N'-di-phenylbenzidine (M1) with maleimide functional group, were developed. Due to the fast Diels-Alder reaction between the maleimide in M1 and the furan group in P1, the blend films of P1 and M1 can be quickly crosslinked in extremely short time, resulting in robust hole transporting layer (HTL) films with good solvent resistance, which can overcome the interface mixing problem in solution processed multilayer PLEDs. Such a moderate cured condition (heated at 150 degrees C for similar to 1 min) can decrease negative effects and the optoelectronic property of the resulting HTL film can be tuned also by changing the ratio of the small molecular crosslinker (5% - 100%; maleimide/furan). The PLEDs, with the structure of ITO/poly(3,4-ethylenedioxythiophene): poly(4-styrenesulfonate) (PEDOT: PSS)/P1 + M1/emmisive layer/Ba/Al, were fabricated to investigate the effects of the crosslinker ratio on device performance. The device study results indicated that the HTLs based on P1 + M1 exhibited excellent hole-transporting/electron blocking properties and can prevent emission quenching caused by PEDOT: PSS in the traditional PEDOT: PSS based PLEDs. When M1 content is below 10%, the device displayed lower V-on, higher B-max and LEmax, and the device with HTL based on P1 + 10% M1 exhibited the best performance with LEmax of 9.0 cd A(-1), B-max of 35681 cd m(-2) and V-on of 3.2 V, with a higher brightness of 5000 cd m(-2). Our results indicated that the Diels-Alder reaction between the maleimide and the furan groups can be used to prepare optoelectronic materials for solution processed multilayer engineering of optoelectronic devices, such as PLEDs, polymer solar cells etc.

Thermally Cross-Linkable Hole-Transporting Materials For Improving Hole Injection In Multilayer Blue-Emitting Phosphorescent Polymer Light-Emitting Diodes

Crosslinkable Hole-Transporting Materials for Solution Processed Polymer Light-Emitting Diodes

Thermally Cross-Linkable Hole-Transporting Materials on Conducting Polymer: Synthesis, Characterization, and Applications for Polymer Light-Emitting Devices

Dual Hole Transport Layers for Blue-Light-emitting PLED: Suppress the Formation of Exciplex Towards High Device Performance and Color Purity

Anionic Triphenylamine‐ and Fluorene‐based Conjugated Polyelectrolyte As a Hole‐transporting Material for Polymer Light‐emitting Diodes

Improving the Performance of Blue Polymer Light-Emitting Diodes Using a Hole Injection Layer with a High Work Function and Nanotexture.

Synthesis of Cross-linkable Hole-transporting Materials Based on Diels-Alder Reaction and Their Application in Polymer Light-emitting Diodes

Solvent Resistant Hole-Transporting Thin Films Via Diacetylene Cross-Linking and Their Applications in Solution-Processed QLEDs

A High Triplet Energy Small Molecule Based Thermally Cross-Linkable Hole-Transporting Material for Solution-Processed Multilayer Blue Electrophosphorescent Devices

Thermally Cross-Linkable Hole-Transport Materials Enable Solution-Processed Blue OLED with LT95 over 150 H

Crosslinkable Triphenylamine-Based Hole-Transporting Polymers for Solution-Processed Polymer Light-Emitting Diodes

High-efficiency Blue-Emitting Organic Light-Emitting Devices with 4, 4′, 4″-Tris(n-carbazolyl)-triphenylamine As the Hole/exciton-Blocking Layer

A Hole-Transporting Material with Controllable Morphology Containing Binaphthyl and Triphenylamine Chromophores

Photocross-Linkable Hole Transport Materials for Inkjet-Printed High-Efficient Quantum Dot Light-Emitting Diodes

Multilayer Blue Polymer Light-Emitting Devices with Spin-Coated Interlayers

Improved efficiency of blue polymer light-emitting diodes using a hole transport material

Enhancing Blue Polymer Light-Emitting Diode Performance by Optimizing the Layer Thickness and the Insertion of a Hole-Transporting Layer

Alkyl fluorene-based cross-linkable hole transport materials with high triplet energy for high-efficiency solution-processed green PHOLEDs

Self‐assembled Electroactive Phosphonic Acids on ITO: Maximizing Hole‐Injection in Polymer Light‐Emitting Diodes

An Efficient Hole-Transporting Blue Fluorophore 3,6-Dipyrenyl-9-ethylcarbazole for Undoped Organic Light-Emitting Devices

Semi-orthogonal Solution-Processed Polyfluorene Derivative for Multilayer Blue Polymer Light-Emitting Diodes