Abstract:Ceria substituted with zirconium (Ce1–x Zr x O2) is a promising material in two-step thermochemical CO2/H2O splitting cycles due to its great oxygen storage capacity and potential fuel production. However, the Ce1–x Zr x O2 solid solution exhibits a relatively slower fuel release rate than cerium oxide alone. Herein, in order to improve the solar-to-fuel energy conversion efficiency, noble metal catalysts (RuO x , PtO x , and IrO x ) are used to boost the CO release rate of Ce0.85Zr0.15O2 (CZ15)-based two-step thermochemical CO2 splitting. Compared with intrinsic Ce0.85Zr0.15O2, the maximal CO release rate can be increased by 35% after loading 0.4 atom % IrO x as a catalyst on the surface of Ce0.85Zr0.15O2. Interestingly, the initial CO release rate can be increased by three times when a small amount of IrO x (1.0 atom %) is doped into the crystal structure of Ce0.85Zr0.15O2 through a solution combustion method. This catalytic effect is ascribed to the increased mixed ionic and electric conductivity within the ceramic bulk and the enhanced chemical reaction rate at the gas–solid interface for iridium-decorated ceria-zirconia solid solution. Our work demonstrates that interface engineering and bulk modification through adding the selected catalyst can effectively enhance the CO2 splitting rate of Ce1–x Zr x O2 oxygen carriers, which provides a promising strategy to promote the fuel release rates of other kinetics-restricted thermochemical CO2/H2O splitting cycles.

Platinum–ceria–zirconia catalysts for hydrogen production in sulfur-iodine cycle

Effects of Ce/Zr Composition on Nickel Based Ce(1−x)ZrxO2 Catalysts for Hydrogen Production in Sulfur–iodine Cycle

Catalytic thermal decomposition of hydrogen iodide in sulfur-iodine cycle for hydrogen production

Effect of preparation method on platinum–ceria catalysts for hydrogen iodide decomposition in sulfur–iodine cycle

Experimental Study on the Catalytic Decomposition of Hydrogen Iodide for SI Thermochemical Cycle

Ceria As a Catalyst for Hydrogen Iodide Decomposition in Sulfur–iodine Cycle for Hydrogen Production

Hydrogen iodide decomposition over nickel–ceria catalysts for hydrogen production in the sulfur–iodine cycle

Hydrogen Production by Hi Decomposition over Nickel-Ceria-Zirconia Catalysts Via the Sulfur-Iodine Thermochemical Water-Splitting Cycle

Experimental Study of Ni/CeO2 Catalytic Properties and Performance for Hydrogen Production in Sulfur–iodine Cycle

Decomposition of Hydrogen Iodide over Pt–Ir/C Bimetallic Catalyst

Influence of the oxidative/reductive treatments on Pt/CeO2 catalyst for hydrogen iodide decomposition in sulfur–iodine cycle

Propene and CO Oxidation on Pt/Ce-Zr-SO 4 2– Diesel Oxidation Catalysts: Effect of Sulfate on Activity and Stability

Catalytic decomposition of hydrogen iodide over pre-treated Ni/CeO2 catalysts for hydrogen production in the sulfur–iodine cycle

Propene and CO oxidation on Pt/Ce-Zr-SO42-diesel oxidation catalysts:Effect of sulfate on activity and stability

The Stability of Pt–Ir/C Bimetallic Catalysts in HI Decomposition of the Iodine–sulfur Hydrogen Production Process

Influence of Ir Content on the Activity of Pt-Ir/C Catalysts for Hydrogen Iodide Decomposition in Iodine–sulfur Cycle

Preparation and Characterization of Hollow Carbon Sphere Supported Catalysts (M@HCS [m=pt, Ir, Ni]) for HI Decomposition in the Iodine–sulfur Cycle for Hydrogen Production

Ceria–Zirconia-Supported Ruthenium Catalysts for Hydrogen Production by Ammonia Decomposition

Platinum Group Metal Catalyst (RuOx, PtOx, and IrOx)-Decorated Ceria-Zirconia Solid Solution as High Active Oxygen Carriers for Solar Thermochemical CO2 Splitting

Metal-Free and Pt-Decorated Graphene-Based Catalysts for Hydrogen Production in a Sulfur–Iodine Thermochemical Cycle

Platinum Group Metal Catalyst (RuO x , PtO x , and IrO x )-Decorated Ceria-Zirconia Solid Solution as High Active Oxygen Carriers for Solar Thermochemical CO 2 Splitting